분말야금 및 주조형 니켈기 초내열합금 크리프 신뢰성의 초음파 모니터링 (Evaluation of Creep Reliability of Powder Metallurgy and Cast-type Ni-based Superalloy by Using Ultrasonic Wave)

서지정보

· 발행기관 : 한국분말재료학회
· 수록지 정보 : 한국분말재료학회지 / 19권 / 3호 / 215 ~ 219페이지
· 저자명 : 최찬양, 송진헌, 오세웅, 김정석, 권숙인, 오승탁, 현창용, 변재원

초록

An attempt was made to evaluate creep reliability of two commercial Ni-based superalloys by using ultrasonic wave. The materials include fine-grained PM alloy fabricated by mechanical alloying and subsequent hot isostatic pressing, and IN738LC cast alloy with a grain size of a few cm. Microstructural parameters (fraction of creep cavity and size of γ' precipitates) and ultrasonic parameters (velocity, attenuation) were measured to try to find relationships between them. Ultrasonic velocity decreased with creep cavity formation in PM alloy. On the other hand, no distinct changing trend of ultrasonic velocity was observed for IN738LC alloy. Ultrasonic attenuation was found to have a linear correlation with the size of γ' precipitates and was suggested as a potential parameter for monitoring creep reliability of IN738LC alloy.

영어초록

An attempt was made to evaluate creep reliability of two commercial Ni-based superalloys by using ultrasonic wave. The materials include fine-grained PM alloy fabricated by mechanical alloying and subsequent hot isostatic pressing, and IN738LC cast alloy with a grain size of a few cm. Microstructural parameters (fraction of creep cavity and size of γ' precipitates) and ultrasonic parameters (velocity, attenuation) were measured to try to find relationships between them. Ultrasonic velocity decreased with creep cavity formation in PM alloy. On the other hand, no distinct changing trend of ultrasonic velocity was observed for IN738LC alloy. Ultrasonic attenuation was found to have a linear correlation with the size of γ' precipitates and was suggested as a potential parameter for monitoring creep reliability of IN738LC alloy.

참고자료

· 없음