미세가공 기술 기반의 마이크로니들 어레이 개발 및 패럴린 적용 가능성에 관한 연구 (Research on the Development of Microneedle Arrays Based on Micromachining Technology and the Applicability of Parylene-C)

서지정보

· 발행기관 : 대한의용생체공학회
· 수록지 정보 : 의공학회지 / 44권 / 6호 / 404 ~ 413페이지
· 저자명 : 김동국, 윤덕규, 이용찬, 김민욱, 노지형, 서요한, 강관수, 정영훈, 김경아, 송태하

초록

In this research, we studied the development of a SUS304 microneedle array based on microfabrication technology and the applicability of Parylene-C thin film, a medical polymer material. First of all, four materials com- monly used in the field of medical engineering (SUS304, Ti, PMMA, and PEEK) were selected and a 5 μm Parylene- C thin film was deposited. The applicability of Parylene-C coating to each material was confirmed through SEM anal- ysis, contact angle measurement, surface roughness(Ra) measurement, and adhesion test according to ASTM stan- dards for each specimen. Parylene-C thin film was deposited based on chemical vapor deposition (CVD), and a 5 μm Parylene-C deposition process was established through trial and error. Through characteristic experiments to confirm the applicability of Parylene-C, SUS304 material, which is the easiest to apply Parylene-C coating without pretreat- ment was selected to develop a microneedle array based on CNC micromachining technology. The CNC microma- chining process was divided into a total of 5 steps, and a microneedle array consisting of 19 needles with an inner diameter of 200 μm, an outer diameter of 400 μm, and a height of 1.4 mm was designed and manufactured. Finally, a 5 μm Parylene-C coated microneedle array was developed, which presented future research directions in the field of microneedle-based drug delivery systems.

영어초록

In this research, we studied the development of a SUS304 microneedle array based on microfabrication technology and the applicability of Parylene-C thin film, a medical polymer material. First of all, four materials com- monly used in the field of medical engineering (SUS304, Ti, PMMA, and PEEK) were selected and a 5 μm Parylene- C thin film was deposited. The applicability of Parylene-C coating to each material was confirmed through SEM anal- ysis, contact angle measurement, surface roughness(Ra) measurement, and adhesion test according to ASTM stan- dards for each specimen. Parylene-C thin film was deposited based on chemical vapor deposition (CVD), and a 5 μm Parylene-C deposition process was established through trial and error. Through characteristic experiments to confirm the applicability of Parylene-C, SUS304 material, which is the easiest to apply Parylene-C coating without pretreat- ment was selected to develop a microneedle array based on CNC micromachining technology. The CNC microma- chining process was divided into a total of 5 steps, and a microneedle array consisting of 19 needles with an inner diameter of 200 μm, an outer diameter of 400 μm, and a height of 1.4 mm was designed and manufactured. Finally, a 5 μm Parylene-C coated microneedle array was developed, which presented future research directions in the field of microneedle-based drug delivery systems.

참고자료

· 없음