0.2% N을 첨가한 수퍼 2상 스테인리스강의 열처리 조건에 따른 특성 평가 - 제1보: 기계적 특성 및 미세조직 (Characteristic Evaluation Based on the Heat Treatment Conditions of Super Duplex Stainless Steel with 0.2% N as an Additive -Part 1: Mechanical Properties and Microstructure)

서지정보

· 발행기관 : 한국해양공학회
· 수록지 정보 : 한국해양공학회지 / 22권 / 4호 / 46 ~ 50페이지
· 저자명 : 안석환, 강홍주, 남기우

초록

Super duplex stainless steel has along life in severe environments because of its strength and corrosion resistance. If 0.2~0.3% Nitrogen in aninterstitial solid solution is added, the austenite structure is reinforced. This improves the solid solution hardening and the anticorrosionability. In this study, the mechanical properties and structures of the super duplex stainless steel with the 0.2% N additive were investigated to determine the effect of various volume fractions on the austenite phase. The various volume fractions and distributions of the austenite structure in the applied test specimenswere obtained by changing the heat treatment temperature and cycle. The characteristics by amounts of the σ phase obtained from the precipitation heat treatment were alsoinvestigated. From the results, when the austenite volume fraction increases, the tensile strength decreases and elongation increases. And the σ phase was rapidly increased by increasing theheat treatment time. When the volume fraction of the σ phase increased, tensile strength increased.

영어초록

Super duplex stainless steel has along life in severe environments because of its strength and corrosion resistance. If 0.2~0.3% Nitrogen in aninterstitial solid solution is added, the austenite structure is reinforced. This improves the solid solution hardening and the anticorrosionability. In this study, the mechanical properties and structures of the super duplex stainless steel with the 0.2% N additive were investigated to determine the effect of various volume fractions on the austenite phase. The various volume fractions and distributions of the austenite structure in the applied test specimenswere obtained by changing the heat treatment temperature and cycle. The characteristics by amounts of the σ phase obtained from the precipitation heat treatment were alsoinvestigated. From the results, when the austenite volume fraction increases, the tensile strength decreases and elongation increases. And the σ phase was rapidly increased by increasing theheat treatment time. When the volume fraction of the σ phase increased, tensile strength increased.

참고자료

· 없음