사출성형 조건 변화에 따른 도광판의 황화현산에 관한 연구 (A study on yellowing property of LGP under various injection molding conditions ))

서지정보

· 발행기관 : 한국금형공학회
· 수록지 정보 : Design & Manufacturing / 9권 / 2호 / 20 ~ 24페이지
· 저자명 : 이성준, 민인기, 김종선, 이성희, 윤경환

초록

Recently, the light guide plate (LGP), a component of the BLU, becomes thinner and larger than ever. In industrial field, specialized injection molding technique is applied to mold the ultra-thin LGP such as a ultra-high speed injection molding. Usually very high melt temperature is used for low viscosity. High injection speed and melt temperature lead to yellowing of LGP. In the present paper a series of injection molding experiment was performed under various injection molding conditions. Yellow index, CIE xy, spectral transmittance of sample were measured using the UV-Visible spectrophotometer. Systematic decrease of spectral transmittance in UV-B range was found as the melt temperature was higher. Yellow index and CIE xy were became higher near the gate location in LGP. From the result of analysis of variance, the main factor to affect for yellow index was mold temperature and that for spectral transmittance(at 315 nm) was melt temperature.

영어초록

Recently, the light guide plate (LGP), a component of the BLU, becomes thinner and larger than ever. In industrial field, specialized injection molding technique is applied to mold the ultra-thin LGP such as a ultra-high speed injection molding. Usually very high melt temperature is used for low viscosity. High injection speed and melt temperature lead to yellowing of LGP. In the present paper a series of injection molding experiment was performed under various injection molding conditions. Yellow index, CIE xy, spectral transmittance of sample were measured using the UV-Visible spectrophotometer. Systematic decrease of spectral transmittance in UV-B range was found as the melt temperature was higher. Yellow index and CIE xy were became higher near the gate location in LGP. From the result of analysis of variance, the main factor to affect for yellow index was mold temperature and that for spectral transmittance(at 315 nm) was melt temperature.

참고자료

· 없음