Al-Si 도금강의 통전 가열에 따른 미세조직과 도금층 변화 (Change in Microstructure and Coating Layer of Al-Si Coated Steel after Conductive Heating)

서지정보

· 발행기관 : 한국열처리공학회
· 수록지 정보 : 열처리공학회지 / 34권 / 3호 / 107 ~ 115페이지
· 저자명 : 정우창

초록

Al-Si coated boron steel has been widely used as commercial hot stamping steel. When the steel is heated at 900~930o C for 5 min in an electric furnace, thickness of the coating layer increases as a consequence of formation of intermetallic compounds and diffusion layer. The diffusion layer plays an important roll in blunting the propagation of crack from coating layer to base steel. Change in microstructure and coating layer of Al-Si coated boron steel after conductive heating with higher heating rate than electric furnace has been investigated in this study. Conductive-heated steel showed the martensitic structure with vickers hardness of 505~567. Both intermetallic compounds in coating layer and diffusion layer were not observed in conductive-heated steel due to rapid heating. It has been found that the conductive-heating consisting of rapid heating to 550o C which is lower than melting point of Al-Si coating layer, slower heating to 900o C, and then 1 min holding at 900o C is effective in forming intermetallic compound in coating layer and diffusion layer

영어초록

Al-Si coated boron steel has been widely used as commercial hot stamping steel. When the steel is heated at 900~930o C for 5 min in an electric furnace, thickness of the coating layer increases as a consequence of formation of intermetallic compounds and diffusion layer. The diffusion layer plays an important roll in blunting the propagation of crack from coating layer to base steel. Change in microstructure and coating layer of Al-Si coated boron steel after conductive heating with higher heating rate than electric furnace has been investigated in this study. Conductive-heated steel showed the martensitic structure with vickers hardness of 505~567. Both intermetallic compounds in coating layer and diffusion layer were not observed in conductive-heated steel due to rapid heating. It has been found that the conductive-heating consisting of rapid heating to 550o C which is lower than melting point of Al-Si coating layer, slower heating to 900o C, and then 1 min holding at 900o C is effective in forming intermetallic compound in coating layer and diffusion layer

참고자료

· 없음