H2O2 첨가제를 이용하여 제작한 WO3 광전극의 광전기화학적 특성 개선 연구 (Improvement of Photoelectrochemical Properties of WO3 Photoelectrode Fabricated by Using H2O2 Additive)

서지정보

· 발행기관 : 대한금속·재료학회
· 수록지 정보 : 대한금속·재료학회지 / 59권 / 3호 / 177 ~ 186페이지
· 저자명 : 전승환, 정현진, 배성찬, 류혁현, 이원재

초록

In this study, we deposited a WO3 thin-film photoelectrode on a fluorine-doped tin oxide (FTO) substrate using a spin-coating method, and we investigated the photocurrent density and dark current density of the WO3 photoelectrode with various amounts of H2O2 additive. The morphological, structural, optical, electrical and photoelectrochemical properties of the WO3 photoelectrode with various amounts of H2O2 additive were analyzed using FE-SEM, XRD, UV-vis spectroscopy, EIS and a three-electrode potentiostat/ galvanostat system, respectively. The amount of H2O2 additive has a large influence on the thickness of the WO3 photoelectrode, XRD (100) peak intensity, light absorption, optical energy bandgap, flat-band potential, donor density value, etc., and thus has a large influence on photoelectrochemical properties. Specifically, the H2O2 additive had a large influence on the growth of the WO3 photoelectrode, and the photocurrent density and dark current density characteristics of the WO3 photoelectrode grown to a uniform and thick thickness were largely improved. As a result, the WO3 photoelectrode fabricated with 0.2 mL of added H2O2 exhibited a high photocurrent density value of 1.17 mA/cm2, which was about 23 times higher than that of the WO3 photoelectrode fabricated without H2O2 additive, and had a dark current density value of a low 0.04 mA/cm2, which was a reduction of about 87%.

영어초록

In this study, we deposited a WO3 thin-film photoelectrode on a fluorine-doped tin oxide (FTO) substrate using a spin-coating method, and we investigated the photocurrent density and dark current density of the WO3 photoelectrode with various amounts of H2O2 additive. The morphological, structural, optical, electrical and photoelectrochemical properties of the WO3 photoelectrode with various amounts of H2O2 additive were analyzed using FE-SEM, XRD, UV-vis spectroscopy, EIS and a three-electrode potentiostat/ galvanostat system, respectively. The amount of H2O2 additive has a large influence on the thickness of the WO3 photoelectrode, XRD (100) peak intensity, light absorption, optical energy bandgap, flat-band potential, donor density value, etc., and thus has a large influence on photoelectrochemical properties. Specifically, the H2O2 additive had a large influence on the growth of the WO3 photoelectrode, and the photocurrent density and dark current density characteristics of the WO3 photoelectrode grown to a uniform and thick thickness were largely improved. As a result, the WO3 photoelectrode fabricated with 0.2 mL of added H2O2 exhibited a high photocurrent density value of 1.17 mA/cm2, which was about 23 times higher than that of the WO3 photoelectrode fabricated without H2O2 additive, and had a dark current density value of a low 0.04 mA/cm2, which was a reduction of about 87%.

참고자료

· 없음