인청동의 전단가공에서 예비 전단가공이 슬리버 발생에 미치는 영향 연구 (A Study on the Effect of Pre-shearing on Sliver Generation in the Shearing of Phosphor Bronze)

서지정보

· 발행기관 : 한국기계기술학회
· 수록지 정보 : 한국기계기술학회지 / 24권 / 5호 / 954 ~ 960페이지
· 저자명 : 신미경, 김병섭, 이춘규

초록

Burr occurs at the bottom of the material as the material breaks during shearing, and sliver occurs in shear droop that occurs when a punch penetrates the surface of the material. Sliver refers to the shape of a long and thin thread, and it is an important defect that can cause a short when assembled into electronic parts other than a defect in the appearance of a product, an assembly defect in the post-process, and an injury to the operator. Sliver does not occur when the molding is completed only by the main shearing without pre-shearing, but sliver occurs when the main shearing is performed after the pre-shearing. The purpose of this study is to study the sliver generation mechanism that occurs during main shearing after pre-shearing. Using the material phosphor bronze C5210-EH(HP), the sliver was observed with the dimensions and stripping force of the pre-shearing as variables, and the effect of the pre-shearing on the sliver was studied. The product used in the experiment is a terminal, a press product that is assembled on a 0.4mm pitch FPC connector. Three experimental variables were selected: the X-axis allowance, the Y-axis length, and the stripping force in the dimensions of the pre-shearing. As a result of 12 experimental conditions, the X-axis allowance had a greater effect on sliver generation than the Y-axis length and stripping force. The cause of sliver during pre-shearing is that the shear droop part is elongated due to bending when the punch is lowered due to the hole in the bottom due to pre-shearing.

영어초록

Burr occurs at the bottom of the material as the material breaks during shearing, and sliver occurs in shear droop that occurs when a punch penetrates the surface of the material. Sliver refers to the shape of a long and thin thread, and it is an important defect that can cause a short when assembled into electronic parts other than a defect in the appearance of a product, an assembly defect in the post-process, and an injury to the operator. Sliver does not occur when the molding is completed only by the main shearing without pre-shearing, but sliver occurs when the main shearing is performed after the pre-shearing. The purpose of this study is to study the sliver generation mechanism that occurs during main shearing after pre-shearing. Using the material phosphor bronze C5210-EH(HP), the sliver was observed with the dimensions and stripping force of the pre-shearing as variables, and the effect of the pre-shearing on the sliver was studied. The product used in the experiment is a terminal, a press product that is assembled on a 0.4mm pitch FPC connector. Three experimental variables were selected: the X-axis allowance, the Y-axis length, and the stripping force in the dimensions of the pre-shearing. As a result of 12 experimental conditions, the X-axis allowance had a greater effect on sliver generation than the Y-axis length and stripping force. The cause of sliver during pre-shearing is that the shear droop part is elongated due to bending when the punch is lowered due to the hole in the bottom due to pre-shearing.

참고자료

· 없음