고신율 금형주조용 Al-9wt%Si-Mg계 합금의 주조특성에 미치는 Fe, Mn함량의 영향 (Effect of Fe, Mn Content on the Castability in Al-9wt%Si-Mg System Alloys for High Elongation)

서지정보

· 발행기관 : 한국주조공학회
· 수록지 정보 : 한국주조공학회지 / 33권 / 6호 / 233 ~ 241페이지
· 저자명 : 김헌주, 정창열

초록

Effect of Fe and Mn contents on the castability of Al-9wt%Si-xMg-yFe-zMn alloy has been studied. The alloy was composed of α-Al phase, Al+eutectic Si phase, β-Al5FeSi compound and chinese script α-Al15(Mn,Fe)3Si2 compound. β-Al5FeSi and α- Al15(Mn,Fe)3Si2 compounds assumed to effect the fluidity and shrinkage behaviors of the alloy during solidification due to the crystallization of α-Al15(Fe,Mn)3Si2 and β-Al5FeSi compounds above eutectic temperature. As Fe and Mn contents of Al-9wt%Si- 0.3wt%Mg system alloy increased from 0.15wt% to 0.6wt% and from 0.3wt% to 0.7wt%, fluidity of the alloy decreased by 5.7% and 3.3%, respectively. And as Mg content of Al-9wt%Si-0.45wt%Fe-0.5wt%Mn system alloy increased from 0.3wt% to 0.4wt%, fluidity of the alloy decreased by 8.6%. When Fe content of the alloy increased from 0.15wt% to 0.6wt%, macro shrinkage ratio decreased from 6.1% to 4.1%, and micro shrinkage ratio increased from 0.04% to 0.24%. Similarly, Mn content of the alloy increased from 0.3wt% to 0.7wt%, macro shrinkage ratio decreased from 6.0% to 4.5% and micro shrinkage ratio increased from 0.12% to 0.18%. Judging from the castability of the alloy, Al-9wt%Si-0.3wt%Mg alloy with low content of Fe and Mn, 0.1wt% Fe and 0.3wt% Mn, is recommendable.

영어초록

Effect of Fe and Mn contents on the castability of Al-9wt%Si-xMg-yFe-zMn alloy has been studied. The alloy was composed ofα-Al phase, Al+eutectic Si phase, β-Al5FeSi compound and chinese script α-Al15(Mn,Fe)3Si2 compound. β-Al5FeSi and α-Al15(Mn,Fe)3Si2 compounds assumed to effect the fluidity and shrinkage behaviors of the alloy during solidification due to the crystallizationof α-Al15(Fe,Mn)3Si2 and β-Al5FeSi compounds above eutectic temperature. As Fe and Mn contents of Al-9wt%Si-0.3wt%Mg system alloy increased from 0.15wt% to 0.6wt% and from 0.3wt% to 0.7wt%, fluidity of the alloy decreased by 5.7%and 3.3%, respectively. And as Mg content of Al-9wt%Si-0.45wt%Fe-0.5wt%Mn system alloy increased from 0.3wt% to 0.4wt%,fluidity of the alloy decreased by 8.6%. When Fe content of the alloy increased from 0.15wt% to 0.6wt%, macro shrinkage ratiodecreased from 6.1% to 4.1%, and micro shrinkage ratio increased from 0.04% to 0.24%. Similarly, Mn content of the alloyincreased from 0.3wt% to 0.7wt%, macro shrinkage ratio decreased from 6.0% to 4.5% and micro shrinkage ratio increased from0.12% to 0.18%. Judging from the castability of the alloy, Al-9wt%Si-0.3wt%Mg alloy with low content of Fe and Mn, 0.1wt% Feand 0.3wt% Mn, is recommendable.

참고자료

· 없음