부품 및 벤치 실험을 통한 폴리우레탄 유압왕복 실의 가속 실험 (Component and Bench Tests of Polyurethane Hydraulic Reciprocating Seal for Accelerated Life Testing)

서지정보

· 발행기관 : 한국트라이볼로지학회
· 수록지 정보 : 한국트라이볼로지학회지 / 30권 / 5호 / 271 ~ 277페이지
· 저자명 : 제영완, 김한솔, 김류운, 정구현, 안중혁, 전홍규

초록

Hydraulic reciprocating seals have been widely used to prevent fluid leakage and to provide lubricantfilm on counter surface in various hydraulic system. The degradation of the seal may cause the catastrophic failureof the hydraulic system. To assess the durability of the seals and the compatibility with counter surface, acceleratedlife testing (ALT) has been typically employed from industry. However, ALT often takes up to a fewmonths to cause a failure of the seals, and therefore, there is a need to develop more efficient ALT methods. Inthis work, the degradation characteristics of polyurethane (PU) seals from field test are investigated and they arecompared to those from the component and bench tests, with an aim to contribute to the development of ALTmethod. From the comparison of the cross-sectional profiles of the sealing surface of the PU specimens beforeand after the tests, both wear and compression set are found to be responsible for degradation of the PU seals.
It is also shown that the major wear mechanisms of the PU seals from the field is abrasive wear and formationof pits. The component and bench tests performed in this work are shown to reproduce such wear mechanisms,and therefore, those test methods can be used as an ALT method for PU seals. In particular, the bench test proposedin this work may be effectively utilized to assess the durability and the compatibility of the seals with thecounter surface. The results of this work are expected to aid in the design of ALT for PU seal.

영어초록

Hydraulic reciprocating seals have been widely used to prevent fluid leakage and to provide lubricantfilm on counter surface in various hydraulic system. The degradation of the seal may cause the catastrophic failureof the hydraulic system. To assess the durability of the seals and the compatibility with counter surface, acceleratedlife testing (ALT) has been typically employed from industry. However, ALT often takes up to a fewmonths to cause a failure of the seals, and therefore, there is a need to develop more efficient ALT methods. Inthis work, the degradation characteristics of polyurethane (PU) seals from field test are investigated and they arecompared to those from the component and bench tests, with an aim to contribute to the development of ALTmethod. From the comparison of the cross-sectional profiles of the sealing surface of the PU specimens beforeand after the tests, both wear and compression set are found to be responsible for degradation of the PU seals.
It is also shown that the major wear mechanisms of the PU seals from the field is abrasive wear and formationof pits. The component and bench tests performed in this work are shown to reproduce such wear mechanisms,and therefore, those test methods can be used as an ALT method for PU seals. In particular, the bench test proposedin this work may be effectively utilized to assess the durability and the compatibility of the seals with thecounter surface. The results of this work are expected to aid in the design of ALT for PU seal.