도로포장 형식별 부착식 도로표지병의 성능 평가 연구 (Performance Evaluation of Adhesive Road Studs for Different Pavement Types)

서지정보

· 발행기관 : 한국도로학회
· 수록지 정보 : 한국도로학회논문집 / 21권 / 6호 / 121 ~ 126페이지
· 저자명 : 박기수, 박원일, 진민수, 이석기, 박희문

초록

PURPOSES: The objective of this study is to evaluate the shear and tensile strength properties of adhesive road studs in asphalt and concrete pavements.
METHODS: The 300 mm×300 mm×50 mm rectangular specimens were fabricated using asphalt and concrete mixture for installation of road studs. Four 140-mm-radius circular areas were milled on each specimen with depth of 5 mm to install the adhesive road studs. About 100 g of thermal melting adhesive was applied on the milled area, and then the road stud was bonded onto the surface of the asphalt and concrete mixture. Direct shear testing was conducted at a speed of 5 mm/min on the interface between road stud and asphalt and concrete materials.
Tensile strength testing was also conducted on the prepared specimens by applying load with increase of 50 kPa per second. These tests were performed not only in dry condition but also in wet condition to determine the effect of moisture on the shear and tensile strengths.
RESULTS : According to the shear testing results, the average shear strength of asphalt samples in dry and wet conditions are 0.509 and 0.234 MPa, respectively. From this testing, the shear strength of wet sample was found to be decreased by 50% with respect to that of the dry sample. Similar trends can be observed on the concrete samples. The average tensile strength of asphalt samples was 0.187 MPa at 1.5 mm of displacement in dry condition. The concrete sample has a 0.222 MPa average tensile strength, which is slightly higher than that of the asphalt sample because of the rough surface characteristics of the concrete sample.
CONCLUSIONS: It is determined from this study that the shear and tensile strengths of road stud bonded on the surface of asphalt mixture are slightly lower than those on concrete samples. Regardless of the pavement type, the wet conditioning of the sample can decrease the shear and tensile strength by 50% those of the dry sample. In the future, the quality improvement of adhesive and increase of specific surface area should be considered to improve the bonding property between road stud and pavement surface.

영어초록

PURPOSES: The objective of this study is to evaluate the shear and tensile strength properties of adhesive road studs in asphalt and concrete pavements.
METHODS: The 300 mm×300 mm×50 mm rectangular specimens were fabricated using asphalt and concrete mixture for installation of road studs. Four 140-mm-radius circular areas were milled on each specimen with depth of 5 mm to install the adhesive road studs. About 100 g of thermal melting adhesive was applied on the milled area, and then the road stud was bonded onto the surface of the asphalt and concrete mixture. Direct shear testing was conducted at a speed of 5 mm/min on the interface between road stud and asphalt and concrete materials.
Tensile strength testing was also conducted on the prepared specimens by applying load with increase of 50 kPa per second. These tests were performed not only in dry condition but also in wet condition to determine the effect of moisture on the shear and tensile strengths.
RESULTS : According to the shear testing results, the average shear strength of asphalt samples in dry and wet conditions are 0.509 and 0.234 MPa, respectively. From this testing, the shear strength of wet sample was found to be decreased by 50% with respect to that of the dry sample. Similar trends can be observed on the concrete samples. The average tensile strength of asphalt samples was 0.187 MPa at 1.5 mm of displacement in dry condition. The concrete sample has a 0.222 MPa average tensile strength, which is slightly higher than that of the asphalt sample because of the rough surface characteristics of the concrete sample.
CONCLUSIONS: It is determined from this study that the shear and tensile strengths of road stud bonded on the surface of asphalt mixture are slightly lower than those on concrete samples. Regardless of the pavement type, the wet conditioning of the sample can decrease the shear and tensile strength by 50% those of the dry sample. In the future, the quality improvement of adhesive and increase of specific surface area should be considered to improve the bonding property between road stud and pavement surface.