열형-롤 각인으로 형성한 Ag 격자 패턴과 전도성 고분자 코팅을 이용한 투명전극 필름 제작에 관한 연구 (Study and Fabrication of Transparent Electrode Film by using Thermal-Roll Imprinted Ag Mesh Pattern and Coated Conductive Polymer)

서지정보

· 발행기관 : 한국정밀공학회
· 수록지 정보 : 한국정밀공학회지 / 27권 / 9호 / 11 ~ 15페이지
· 저자명 : 유종수, 조정대, 윤성만, 김도진

초록

In this study, to fabricate a low-resistance and high optical transparency electrode film, the following steps were performed: the design and manufacture of electroforming stamp, the fabrication of a thermal roll-imprinted polycarbonate (PC) patterned films, the filled low-resistance Ag paste using doctor blade process on patterned PC films and spin coating by conductive polymers. As a result of PC films imprinted line width of 26.69±2 μm, channel length of 245.57±2μm, and pattern depth of 7.54±0.2 μm. Ag paste to fill part of the patterned film with conductive polymer coating and then the following parameters were obtained: a sheet resistance of 11.1Ω/sq, optical transparency values at a wavelength of 550 nm was 80.31 %.

영어초록

In this study, to fabricate a low-resistance and high optical transparency electrode film, the following steps were performed: the design and manufacture of electroforming stamp, the fabrication of a thermal roll-imprinted polycarbonate (PC) patterned films, the filled low-resistance Ag paste using doctor blade process on patterned PC films and spin coating by conductive polymers. As a result of PC films imprinted line width of 26.69±2 μm, channel length of 245.57±2μm, and pattern depth of 7.54±0.2 μm. Ag paste to fill part of the patterned film with conductive polymer coating and then the following parameters were obtained: a sheet resistance of 11.1Ω/sq, optical transparency values at a wavelength of 550 nm was 80.31 %.

참고자료

· 없음