캡슐형 치과용 아말감의 보관 온도에 따른 수은 증기 누출에 관한 연구 (A study on the leakage of mercury vapor from pre-capsulated dental amalgam according to storage temperature)

서지정보

· 발행기관 : 대한치과의사협회
· 수록지 정보 : 대한치과의사협회지 / 60권 / 6호 / 341 ~ 348페이지
· 저자명 : 김지은, 서영빈, 권재성, 김광만

초록

Objective: The aim of this study was to measure the amount of mercury vapor from one pre-capsulated dental amalgam ac cording to the storage temperature and to investigate whether the storage temperature suggested by the manufacturer or ISO is appropriate for the storage.
Materials and Methods: GK Amalgam and Ultracaps+ were used in this study. One pre-capsulated dental amalgam was placed in a Tedlar Bag and the Tedlar Bag was filled with 2 L of (4±2) ℃ air. The Tedler Bag was stored at one of the three different temperature conditions; (4±2) ℃, (23±2) ℃ and (30±2) ℃ for 24 hours. By applying Ontario hydro method, mercury vapor in the Tedlar Bag was oxidized in KMnO4-H2SO4 solvent and pre-treated, followed by analyses using the Cold Vapor Atomic Absorption Spectrophotometry. Five measurements were obtained from each group.
Results: The average mercury vapor from GK Amalgam was (0.068±0.024), (0.300±0.100) and (0.544±0.133) mg/m3 , and Ul tracaps+ was (0.026±0.008), (0.088±0.013) and (0.146±0.023) mg/m3 at (4±2) ℃, (23±2) ℃ and (30±2), respectively. There was a significant difference between GK Amalgam and Ultracaps+ at each temperature, and depending on the storage temperature in each material (p<0.05).
Conclusions: It was evident that storage at (23±2) ℃ result in exposure of mercury vapor exceeding 340 to 1,170% of the expo sure amount compare to the standard set by the Ministry of Labor in Korea. In order to reduce the amount of mercury vapor leaking from pre-capsulated dental amalgam, it is considered an effective method for users to periodically ventilate storage places, store them in refrigerators or keepin sealed container, and manufacturers to produce them in individual packaging.

영어초록

Objective: The aim of this study was to measure the amount of mercury vapor from one pre-capsulated dental amalgam ac cording to the storage temperature and to investigate whether the storage temperature suggested by the manufacturer or ISO is appropriate for the storage.
Materials and Methods: GK Amalgam and Ultracaps+ were used in this study. One pre-capsulated dental amalgam was placed in a Tedlar Bag and the Tedlar Bag was filled with 2 L of (4±2) ℃ air. The Tedler Bag was stored at one of the three different temperature conditions; (4±2) ℃, (23±2) ℃ and (30±2) ℃ for 24 hours. By applying Ontario hydro method, mercury vapor in the Tedlar Bag was oxidized in KMnO4-H2SO4 solvent and pre-treated, followed by analyses using the Cold Vapor Atomic Absorption Spectrophotometry. Five measurements were obtained from each group.
Results: The average mercury vapor from GK Amalgam was (0.068±0.024), (0.300±0.100) and (0.544±0.133) mg/m3 , and Ul tracaps+ was (0.026±0.008), (0.088±0.013) and (0.146±0.023) mg/m3 at (4±2) ℃, (23±2) ℃ and (30±2), respectively. There was a significant difference between GK Amalgam and Ultracaps+ at each temperature, and depending on the storage temperature in each material (p<0.05).
Conclusions: It was evident that storage at (23±2) ℃ result in exposure of mercury vapor exceeding 340 to 1,170% of the expo sure amount compare to the standard set by the Ministry of Labor in Korea. In order to reduce the amount of mercury vapor leaking from pre-capsulated dental amalgam, it is considered an effective method for users to periodically ventilate storage places, store them in refrigerators or keepin sealed container, and manufacturers to produce them in individual packaging.