성견에서 즉시 임플란트 식립시 국내 임플란트에서의 골 유착반응에 관한 연구 (Study on Osseointegration of the Immediate Placement Using Korean Implant Systems in Beagle Dog)

서지정보

· 발행기관 : 대한치주과학회
· 수록지 정보 : Journal of Periodontal & Implant Science / 37권 / 2호 / 223 ~ 236페이지
· 저자명 : 서정윤, 이욱재, 이종철, 신미란, 김윤상, 피성희, 신형식, 유형근

초록

This study was attempted to evaluate home-manufactured implants by placing Stage-1Ⓡ Implant (Lifecore. Co., USA) whose surface is treated with RBM that has already been varified clinically, ChaorumⓇ Implant(Chaorum Co., Korea) whose surface treatment is same as that of Stage-1 Implant and AtlasⓇ Implant(Cewellmedi Co., Korea) whose surface is treated with anodic oxidation immediately after the teeth of experimental animals were extracted to compare histological findings among them. Stage-1 Implant(diameter: 3.5mm, length: 10mm), Chaorum Implant(diameter: 3.3mm, length: 8.5mm) and Cowell medi Implant(diameter: 4.0mm, length: 8.0mm) were placed into the mandible premolars of 2 adult beagle dogs immediately after their teeth were extracted, and then histological findings were analyzed at 6 weeks. After those implants were inserted directly after their teeth were extracted, the results of periotest were recorded, radiography was done, the subjects went through thorough control for 6 weeks, and then comparison among periotest, radiography and histological finding was made. After comparison of those findings, the values of periotest were satisfactory and bone healing was relatively satisfactory on radiography at 6 weeks. For osseointegration with the bone tissue, Stage-1 was 45.3%, Chaorum 55.3%, and Cowellmedi 52.5%, which was a satisfactory result. Although implant surgery immediately after teeth were extracted involves difficulties among recent implant surgeries, it is being frequently used in that it may reduce surgery hours, the frequency of surgery, and bone loss for patients. This experiment was conducted to evaluate the technological levels of home-manufactured implants that have been remarkably developed in recent years and in conclusion, those implants showed nearly similar result.

영어초록

This study was attempted to evaluate home-manufactured implants by placing Stage-1Ⓡ Implant (Lifecore. Co., USA) whose surface is treated with RBM that has already been varified clinically, ChaorumⓇ Implant(Chaorum Co., Korea) whose surface treatment is same as that of Stage-1 Implant and AtlasⓇ Implant(Cewellmedi Co., Korea) whose surface is treated with anodic oxidation immediately after the teeth of experimental animals were extracted to compare histological findings among them. Stage-1 Implant(diameter: 3.5mm, length: 10mm), Chaorum Implant(diameter: 3.3mm, length: 8.5mm) and Cowell medi Implant(diameter: 4.0mm, length: 8.0mm) were placed into the mandible premolars of 2 adult beagle dogs immediately after their teeth were extracted, and then histological findings were analyzed at 6 weeks. After those implants were inserted directly after their teeth were extracted, the results of periotest were recorded, radiography was done, the subjects went through thorough control for 6 weeks, and then comparison among periotest, radiography and histological finding was made. After comparison of those findings, the values of periotest were satisfactory and bone healing was relatively satisfactory on radiography at 6 weeks. For osseointegration with the bone tissue, Stage-1 was 45.3%, Chaorum 55.3%, and Cowellmedi 52.5%, which was a satisfactory result. Although implant surgery immediately after teeth were extracted involves difficulties among recent implant surgeries, it is being frequently used in that it may reduce surgery hours, the frequency of surgery, and bone loss for patients. This experiment was conducted to evaluate the technological levels of home-manufactured implants that have been remarkably developed in recent years and in conclusion, those implants showed nearly similar result.

참고자료

· 없음