Effects of Mechanically Activated Milling and Calcination Process on the Phase Stability and Particle Morphology of Monoclinic Zirconia Synthesized by Hydrolysis of ZrOCl2 Solution

서지정보

· 발행기관 : 한국재료학회
· 수록지 정보 : 한국재료학회지 / 23권 / 10호
· 저자명 : Lee, Young-Geun, Ur, Soon-Chul, Mahmud, Iqbal, Yoon, Man-Soon

영어초록

The purpose of this paper was to investigate the effect of a high-energy milling (HEM) process on the particle morphology and the correlation between a thermal treatment and tetragonal/monoclinic nanostructured zirconia powders obtained by a precipitation process. To eliminate chloride residue ions from hydrous zirconia, a modified washing method was used. It was found that the used washing method was effective in removing the chloride from the precipitated gel. In order to investigate the effect of a pre-milling process on the particle morphology of the precipitate, dried Zr(OH)4 was milled using a HEM machine with distilled water. The particle size of the Zr(OH)4 powder exposed to HEM reduced to 100~150 nm, whereas that of fresh Zr(OH)4 powder without a pre-milling process had a large and irregular size of 100 nm~1.5 μm. Additionally, modified heat treatment process was proposed to achieve nano-sized zirconia having a pure monoclinic phase. It was evident that two-step calcining process was effective in perfectly eliminating the tetragonal phase, having a small average particle of ~100 nm with good uniformity compared to the sample calcined by a single-step process, showing a large average particle size of ~300 nm with an irregular particle shape and a broad particle size distribution. The modified method is considered to be a promising process for nano-sized zirconia having a fully monoclinic phase.

참고자료

· 없음