CaWO4:Eu3+ 형광체의 합성과 발광 특성
(주)코리아스칼라
- 최초 등록일
- 2016.04.02
- 최종 저작일
- 2012.05
- 5페이지/ 어도비 PDF
- 가격 4,000원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국재료학회
ㆍ수록지정보 : 한국재료학회지 / 22권 / 5호
ㆍ저자명 : 조신호, 조선욱
영어 초록
Red phosphors Ca1-1.5xWO4:Eux3+ were synthesized with different concentrations of Eu3+ ions by using a solid-statereaction method. The crystal structure of the red phosphors was found to be a tetragonal system. X-ray diffraction (XRD) resultsshowed the (112) main diffraction peak centered at 2θ=28.71o, and the size of crystalline particles exhibited an overalldecreasing tendency according to the concentration of Eu3+ ions. The excitation spectra of all the phosphors were composedof a broad band centered at 275nm in the range of 230-310nm due to O2−→W6+ and a narrow band having a peak at 307nmcaused by O2−→Eu3+. Also, the excitation spectrum presents several strong lines in the range of 305-420nm, which areassigned to the 4f-4f transitions of the Eu3+ ion. In the case of the emission spectrum, all the phosphor powders, irrespectiveof Eu3+ ion concentration, indicated an orange emission peak at 594nm and a strong red emission spectrum centered at 615nm,with two weak lines at 648 and 700nm. The highest red emission intensity occurred at x=0.10mol of Eu3+ ion concentrationwith an asymmetry ratio of 12.5. Especially, the presence of Eu3+ in the Ca1-1.5xWO4:Eux3+ shows very effective use of excitationenergy in the range of 305-420nm, and finally yields a strong emission of red light.
참고 자료
없음
"한국재료학회지"의 다른 논문
더보기 (2/7)