열처리 온도 및 분위기에 따른 다공질 실리콘의 구조 및 광학적 특성 (Effects of Annealing Temperature and Atmosphere on Properties of Porous Silicon)

서지정보

· 발행기관 : 한국전기전자재료학회
· 수록지 정보 : 전기전자재료학회논문지 / 23권 / 8호 / 581 ~ 586페이지
· 저자명 : 최현영, 임광국, 전수민, 조민영, 김군식, 김민수, 이동율, 김진수, 김종수, 임재영

초록

The porous Si (PS) was annealed at various temperature in air, argon, and nitrogen atmosphere. Structural and optical properties of the annealed PS were investigated by scanning electron microscopy (SEM) and photoluminescence (PL). It is found that the shape of pore is changed from circle to channel as increasing annealing temperature which was annealed in air and argon atmosphere. In case of PS annealed in nitrogen atmosphere, the shape of pore is changed from channel to circle with increase annealing temperature from 600 to 800℃. The PL peak position is blue-shifted with increasing annealing temperature. As annealing temperature increases, the PL intensity of the PS annealed in argon is decreased but that of the PS annealed in nitrogen is increased. It might be due to the formation of Si-N bonds and it passivates the non-radiative centers which is Si dangling bonds on the surface of the PS.

영어초록

The porous Si (PS) was annealed at various temperature in air, argon, and nitrogen atmosphere. Structural and optical properties of the annealed PS were investigated by scanning electron microscopy (SEM) and photoluminescence (PL). It is found that the shape of pore is changed from circle to channel as increasing annealing temperature which was annealed in air and argon atmosphere. In case of PS annealed in nitrogen atmosphere, the shape of pore is changed from channel to circle with increase annealing temperature from 600 to 800℃. The PL peak position is blue-shifted with increasing annealing temperature. As annealing temperature increases, the PL intensity of the PS annealed in argon is decreased but that of the PS annealed in nitrogen is increased. It might be due to the formation of Si-N bonds and it passivates the non-radiative centers which is Si dangling bonds on the surface of the PS.

참고자료

· 없음