TiC 분산된 니켈기 합금의 미세조직 및 기계적 특성에 미치는 열처리 영향
(주)코리아스칼라
- 최초 등록일
- 2016.04.01
- 최종 저작일
- 2002.12
- 8페이지/ 어도비 PDF
- 가격 4,000원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국분말야금학회
ㆍ수록지정보 : 한국분말야금학회지 / 9권 / 6호
ㆍ저자명 : 홍성현, 황금철, 이원혁, 진억용
영어 초록
The microstructures and properties of TiC dispersed nickel-base alloy were studied in this work. The alloy prepared by powder metallurgical processing was solution treated, 1st-aged at for 16 hours, and then 2nd-aged at for 4 hours. Microstucture of sintered specimen showed that TiC particles are uniformly dispersed in Ni base alloy. In the specimen aged at for 8 hours, the fine (Al,Ti) precipitates with round shape are observed and the very fine (Al,Ti) particles with round shape are precipitated in the specimen aged at for 4 hours. The presence of precipitates in TiC/Ni base alloy increased the hardness and wear resistance of the specimen. The hardness and wear resistance of the Ni-base with TiC are higher than those of conventional Ni-base superalloy X-750 because of dispersion strengthening of TiC particles. The hardness, transverse rupture strength and resistance of the specimen 2nd-aged at for 4 hours are higher than those of 1st-aged specimen due to ultrafine (Al,Ti) precipitates.
참고 자료
없음
"한국분말야금학회지"의 다른 논문
더보기 (4/9)