Kinetics of Thermal Degradation of Polypropylene/Nanoclay/Wood Flour Nanocomposites
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국유화학회
ㆍ수록지정보 : 韓國油化學會誌 / 24권 / 3호
ㆍ저자명 : D. Jagan Mohan, Sun-Young Lee, In-Aeh Kang, Geum-Hyun Doh, Byung-Dae Park, Qinglin Wu
ㆍ저자명 : D. Jagan Mohan, Sun-Young Lee, In-Aeh Kang, Geum-Hyun Doh, Byung-Dae Park, Qinglin Wu
영어 초록
As a part of enhancing the performance of wood-plastic composites (WPC), polypropylene (PP)/ nanoclay (NC)/ wood flour (WF) nanocomposites were prepared using melt blending and injection molding process to evaluate their thermal stability. Thermogravimetric analysis (TGA) was employed to investigate thermal degradation kinetics of the nanocomposites both dynamic and isothermal conditions. Dynamic scans of the TGA showed an increased thermal stability of the nanocomposites at moderate wood flour concentrations (up to 20 phr, percentage based on hundred percent resin) while it decreased with the addition of 30 phr wood flour. The activation energy (Ea) of thermal degradation of nanocomposites increased when nanoclay was added and the concentration of wood flour increased. Different equations were used to evaluate isothermal degradation kinetics using the rate of thermal degradation of the composites, expressed as weight loss (%) from their isothermal TGA curves. Degradation occurred at faster rate in the initial stages of about 60 min., and then proceeded in a gradual manner. However, nanocomposites with wood flour of 30 phr heated at 300℃ showed a drastic difference in their degradation behavior, and reached almost a complete decomposition after 40 min. of the isothermal heating. The degree of decomposition was greater at higher temperatures, and the residual weight of isothermal degradation of nanocomposites greatly varied from about 10 to 90%, depending on isothermal temperatures. The isothermal degradation of nanocomposites also increased their thermal stability with the addition of 1 phr nanoclay and of wood flour up to 20 phr. But, the degradation of PP100/NC1/MAPP3/WF30 nanocomposites with 30 phr wood flour occurs at a faster rate compared to those of the others, indicating a decrease in their thermal stability.참고 자료
없음태그
"韓國油化學會誌"의 다른 논문
- Cyclotetramethylene-tetranitramine의 미세 입자 제조를 위한 결정화 연구14페이지
- 페로브스카이트 촉매에서 A-Site 치환에 따른 촉매활성 변화6페이지
- 졸-겔 법에 의한 구형 미분체 Barium Titanate의 제조7페이지
- 용매 증발법에 의한 YGdO3:Eu3+ 형광체의 제조와 발광 특성8페이지
- TiO2를 이용한 메틸메르캅탄의 광촉매 분해메커니즘5페이지
- 폐놀계 화합물과 포름알데히드의 축합반응으로부터 노볼락 레진의 합성10페이지
- 마늘 추출물의 약리적 특성 및 분석8페이지
- 난연도료용 트리포스포러스 함유 변성폴리에스테르의 합성9페이지
- 수용성 절삭유의 Copper Alloy Metal Fiber에 의한 항균 특성에 관한 연구5페이지
- Mechanical Properties of Vapor Grown Carbon Fiber/Epoxy..8페이지