저온 분사 공정으로 제조된 티타늄 코팅층의 치밀화에 미치는 열처리 분위기의 영향
(주)코리아스칼라
- 최초 등록일
- 2016.04.01
- 최종 저작일
- 2012.04
- 7페이지/ 어도비 PDF
- 가격 4,000원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국분말야금학회
ㆍ수록지정보 : 한국분말야금학회지 / 19권 / 2호
ㆍ저자명 : 유지상, 김형준, 오익현, 이기안
영어 초록
This study investigated the effects of annealing environment for the densification and purification properties of pure titanium coating layer manufactured by cold spraying. The annealing was conducted at /1 h and three kinds of environments of vacuum, Ar gas, and mixture gas were controlled. Cold sprayed Ti coating layer (as sprayed) represented 6.7% of porosity and 228 HV of hardness, showing elongated particle shapes (severe plastic deformation) perpendicular to injection direction. Regardless of gas environments, all thermally heat treated coating layers consisted of pure -Ti and minimal oxide. Vacuum environment during heat treatment represented superior densification properties (3.8% porosity, 156.7 HV) to those of Ar gas (5.3%, 144.5 HV) and mixture gas (5.5%, 153.1 HV). From the results of phase analysis (XRD, EPMA, SEM, EDS), it was found that the vacuum environment during heat treatment could be effective for reducing oxide contents (purification) in the Ti coating layer. The characteristic of microstructural evolution with heat treatment was found to be different at three different gas environments. The controlling method for improving densification and purification in the cold sprayed Ti coating material was also discussed.
참고 자료
없음
"한국분말야금학회지"의 다른 논문
더보기 (3/8)