고기능성 세라믹 주형 및 중자 제작을 위한 3원계 무기 바인더 시스템 개발
(주)코리아스칼라
- 최초 등록일
- 2023.04.03
- 최종 저작일
- 2022.12
- 7페이지/ 어도비 PDF
- 가격 4,000원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국재료학회
ㆍ수록지정보 : 한국재료학회지 / 32권 / 12호
ㆍ저자명 : 박혜영, 조근호, 최현희, 김봉구, 김은희, 양승철, 정연길
목차
Abstract
1. 서 론
2. 실험방법
2.1. 습식공정을 적용한 세라믹 주형 및 중자 제조
2.2. 건식공정을 적용한 세라믹 주형 및 중자 제조
2.3. 특성평가
3. 실험결과
4. 결 론
Acknowledgement
References
영어 초록
In existing ceramic mold manufacturing processes, inorganic binder systems (Si-Na, two-component system) are applied to ensure the effective firing strength of the ceramic mold and core. These inorganic binder systems makes it possible to manufacture a ceramic mold and core with high dimensional stability and effective strength. However, as in general sand casting processes, when molten metal is injected at room temperature, there is a limit to the production of thin or complex castings due to reduced fluidity caused by the rapid cooling of the molten metal. In addition, because sodium silicate generated through the vitrification reaction of the inorganic binder is converted into a liquid phase at a temperature of 1,000 °C. or higher, it is somewhat difficult to manufacture parts through high-temperature casting. Therefore, in this study, a high-strength ceramic mold and core test piece with effective strength at high temperature was produced by applying a Si-Na-Ti three-component inorganic binder. The starting particles were coated with binary and ternary inorganic binders and mixed with an organic binder to prepare a molded body, and then heat-treated at 1,000/1,350/1,500 °C to prepare a fired body. In the sample where the two-component inorganic binder was applied, the glass was liquefied at a temperature of 1,000 °C or higher, and the strength decreased. However, the firing strength of the ceramic mold sample containing the three-component inorganic binder was improved, and it was confirmed that it was possible to manufacture a ceramic mold and core via high temperature casting.
참고 자료
없음
"한국재료학회지"의 다른 논문
더보기 (2/7)