도로 융설체 개발을 위한 탄소나노튜브-시멘트 복합체 특성에 관한 실험적 연구
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국도로학회
ㆍ수록지정보 : 한국도로학회논문집 / 15권 / 2호
ㆍ저자명 : 허진녕, 박범진, 김태형
ㆍ저자명 : 허진녕, 박범진, 김태형
영어 초록
PURPOSES : This study aims to review the possibility of developing a road snow-melting system that can prevent slip accidents by maintaining a constant temperature of the winter roads and enhance performance of structures, including improvement of compressive strength by mixing carbon nanotube (hereafter referred to as CNT) with cement paste, the basic material. METHODS : To achieve the above purpose, an experiment was conducted by mixing power-type CNT and wrap-type CNT up to cement paste formulation by weight of 0.0wt%~4.1wt% in accordance with "KS L ISO 679(of cement strength test method)", and compressive strength was measured at 28 days of curing. In addition, the volume resistivity of the specimen was measured to test thermal and electrical characteristics, and the rate of temperature changes in specimen surface by power consumption was measured by passing electricity through the cross-sections of the specimen. Meanwhile, the criteria for checking the performance as a road snow-melting system was determined as volume resistivity of 100Ω·cm or less. RESULTS : A comparative analysis between specimen with 0wt% CNT content in plain status and specimen containing various types of CNTs was carried out. From its results, it was found that compressive strength increased approximately 19%, showing the highest rate when 0.2wt% of wrap-type CNT was contained, but volume resistivity of 100Ω·cm or less appeared only in specimens containing more than 0.2wt% CNT. In addition, it was observed that the surface temperature increased by 4.62℃ per minute on average in specimens containing 3.2wt% CNT. CONCLUSIONS : In this study, CNT was examined as an underlying material for a road snow-melting system, and the possibility of developing the road now-melting system was reviewed by conducting various experiments using CNT-Cement composites. From the experimental results, the specimens were found to have a superior performance when compared to the existing road snow-melting systems that place the heat transfer medium such as copper on the road. However, satisfactory strength performance were not obtained from the specimen containing CNT(2.0% or more) that functions as a heating element, which leads to the need for reviewing methods to increase the strength by using plasticizer or admixture.참고 자료
없음"한국도로학회논문집"의 다른 논문
- 매설용 전기 발열 매시의 융설 효과에 대한 현장 적용성 연구9페이지
- 탄소포집 활성 고로슬래그 모르타르의 기초특성에 관한 연구9페이지
- 한국 도로 자본이 산업에 미친 영향과 생산성 분석13페이지
- 미시적 시뮬레이션을 이용한 중앙버스전용차로 효과분석9페이지
- 편익과 비용 분석을 통한 소형차전용지하차도 도입에 관한 연구9페이지
- 고속도로에서 발생한 2차 교통사고의 특성분석9페이지
- Tobit 모형을 이용한 간선도로 사고 요인 분석8페이지
- 국내 로터리의 연령대별 사고모형9페이지
- 폴리우레탄 바인더를 활용한 친환경 도로포장용 혼합물 개발7페이지
- 도로하부 매설관의 매설심도 및 되메우기 재료가 포장체에 미치는 영향 평가8페이지