급속응고된 Al81-(x+y)Si19NixCey 합금의 나노조직과 기계적 특성
(주)코리아스칼라
- 최초 등록일
- 2016.04.01
- 최종 저작일
- 2003.12
- 9페이지/ 어도비 PDF
- 가격 4,000원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국분말야금학회
ㆍ수록지정보 : 한국분말야금학회지 / 10권 / 6호
ㆍ저자명 : 이태행, 홍순직
영어 초록
In order to produce good wear resistance powder metallurgy Al-Si alloys with high strength, addition of glass forming elements of Ni and Ce in Si alloy was examined using SEM, TEM, tensile strength and wear testing. The solubility of Si in aluminum increased with increasing Ni and Ce contents for rapidly solidified powders. These bulk alloys consist of a mixed structure in which fine Si particles with a particle size below 500 nm and very fine A1Ni, A1Ce compounds with a particle size below 200 nm are homogeneously dispersed in aluminum matrix with a grain size below 600 nm. The tensile strength at room temperature for Si, SiNiCe, and SiNiCe bulk alloys extruded at 674 K and ratio of 10 : 1 is 281,521, and 668 ㎫ respectively. Especially, SiNiCe bulk alloy had a high tensile strength of 730 ㎫. These bulk alloys are good wear-resistance bel ter than commercial I/M 390-T6. Specially, attactability for counterpart is very little, about 15 times less than that of the I/M 390-T6. The structural refinement by adding glass forming elements such as Ni and Ce to hyper eutectic Si alloy is concluded to be effective as a structural modification method.d.tion method.d.
참고 자료
없음
"한국분말야금학회지"의 다른 논문
더보기 (5/10)