보통 포틀랜드 콘크리트 기반 교면포장 재료 성능 평가
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국도로학회
ㆍ수록지정보 : 한국도로학회논문집 / 19권 / 6호
ㆍ저자명 : 남정희, 전성일, 권수안
ㆍ저자명 : 남정희, 전성일, 권수안
영어 초록
PURPOSES : The purpose of this study is to develop bridge deck concrete materials based on ordinary Portland cement concrete, and to evaluate the applicability of the developed materials through material properties tests.METHODS : For field implementation, raw material (cement, fine aggregate, and coarse aggregate) properties, fresh concrete properties (slump and air content), strength (compressive, flexural and bond strength) gain, and durability (freeze-thaw resistance, scaling resistance, and rapid chloride penetrating resistance) performance were evaluated in the laboratory.RESULTS: For the selected binder content of 410 kg/m3, W/B = 0.42, and S/a = 0.48, the following material performance results were obtained. Considering the capacity of the deck finisher, a minimum slump of 150 mm was required. At least 6 % of air content was obtained to resist freezethaw damage. In terms of strength, 51.28 MPa of compressive strength, 7.41 MPa of flexural strength, and 2.56 MPa of bond strength at 28 days after construction were obtained. A total of 94.9 % of the relative dynamic modulus of elasticity after 300 cycles of freeze-thaw resistance testing and 0.0056 kg/m2 of weight loss in a scaling resistance test were measured. However, in a chloride ion penetration resistance test, the result of 3,356 Coulomb, which exceeds the threshold value of the standard specification (1000 Coulomb at 56 days) was observed.CONCLUSIONS: Instead of using high-performance modified bridge deck materials such as latex or silica fume, we developed an optimum mix design based on ordinary Portland cement concrete. A test construction was carried out at ramp bridge B (bridge length = 111 m) in Gim Jai City. Immediately after the concrete was poured, the curing compound was applied, and then wet mat curing was applied for 28 days. Considering the fact that cracks did not occur during the monitoring period, the applicability of the developed material is considered to be high.참고 자료
없음태그
"한국도로학회논문집"의 다른 논문
- 산업단지 유형에 따른 교통사고 특성 비교 분석12페이지
- 자동차와 자전거 간 추월 최소요구 이격거리 추정 방법론 연구9페이지
- 확률기반 비신호교차로의 우회전 전용차로 설치 기준 정립8페이지
- 연속류 위험도로구간에서의 운전자의 도로속도규정 준수에 따른 온실가스 변화량 연구8페이지
- 조도 기반 자동차 전조등 시인 성능 평가 방법의 적정성 평가9페이지
- 도심부 도로 기능별 위계 재편에 관한 연구 : 부산광역시 서면 도심을 중심으로10페이지
- 연속류 도로구간의 수막정보 발생구간 추정 및 적용연구7페이지
- 드라이빙 시뮬레이터 주행과 현장주행시 운전자 반응 비교 연구7페이지
- 도로함몰관리체계 구성요소 최적화방안 연구11페이지
- 현장 및 실내조사를 통한 일반국도교량의 화재위험요소 분석11페이지