텅스텐 산화물의 환원을 이용한 나노/마이크로 크기 텅스텐 혼합분말 제조
(주)코리아스칼라
- 최초 등록일
- 2023.04.05
- 최종 저작일
- 2017.10
- 5페이지/ 어도비 PDF
- 가격 4,000원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국재료학회
ㆍ수록지정보 : 한국재료학회지 / 27권 / 10호
ㆍ저자명 : 권나연, 정영근, 오승탁
영어 초록
An optimum route to fabricate a hybrid-structured W powder composed of nano and micro size powders was investigated. The mixture of nano and micro W powders was prepared by a ball milling and hydrogen reduction process for WO3 and W powders. Microstructural observation for the ball-milled powder mixtures revealed that the nano-sized WO3 particles were homogeneously distributed on the surface of large W powders. The reduction behavior of WO3 powder was analyzed by a temperature programmed reduction method with different heating rates in Ar-10% H2 atmosphere. The activation energies for the reduction of WO3, estimated by the slope of the Kissinger plot from the amount of reaction peak shift with heating rates, were measured as 117.4 kJ/mol and 94.6 kJ/mol depending on reduction steps from WO3 to WO2 and from WO2 to W, respectively. SEM and XRD analysis for the hydrogen-reduced powder mixture showed that the nano-sized W particles were well distributed on the surface of the micro-sized W powders.
참고 자료
없음
"한국재료학회지"의 다른 논문
더보기 (4/9)