진공자외선 여기에 의한 YAGG:Ce3+ 형광체의 광발광 특성에 미치는 Al2O3 나노입자 원료의 결정상의 영향
(주)코리아스칼라
- 최초 등록일
- 2016.04.02
- 최종 저작일
- 2012.04
- 7페이지/ 어도비 PDF
- 가격 4,000원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국재료학회
ㆍ수록지정보 : 한국재료학회지 / 22권 / 4호
ㆍ저자명 : 우미혜, 최성호, 정하균
영어 초록
Ce3+-doped yttrium aluminum gallium garnet (YAGG:Ce3+), which is a green-emitting phosphor, was synthesizedby solid state reaction using α-phase or γ-phase of nano-sized Al2O3 as the Al source. The processing conditions and thechemical composition of phosphor for the maximum emission intensity were optimized on the basis of emission intensity undervacuum UV excitation. The optimum heating temperature for phosphor preparation was 1550oC. Photoluminescence propertiesof the synthesized phosphor were investigated in detail. From the excitation and emission spectra, it was confirmed that theYAGG:Ce3+ phosphors effectively absorb the vacuum UV of 120-200nm and emit green light positioned around 530nm. Thecrystalline phase of the alumina nanoparticles affected the particle size and the luminescence property of the synthesizedphosphors. Nano-sized γ-Al2O3 was more effective for the achievement of higher emission intensity than was nano-sized α-Al2O3. This discrepancy is considered to be because the diffusion of Al3+ into Y2O3 lattice is dependent on the crystalline phaseof Al2O3, which affects the phase transformation of YAGG:Ce3+ phosphors. The optimum chemical composition, having themaximum emission intensity, was (Y2.98Ce0.02)(Al2.8Ga1.8)O11.4 prepared with γ-Al2O3. On the other hand, the decay time of theYAGG:Ce3+ phosphors, irrespective of the crystalline phase of the nano-sized alumina source, was below 1 ms due to theallowed 5d→4f transition of the Ce3+ activator.
참고 자료
없음
"한국재료학회지"의 다른 논문
더보기 (3/8)