열경화성 수지의 축중합에 의한 고밀도 유리상 탄소의 제조
(주)코리아스칼라
- 최초 등록일
- 2016.04.02
- 최종 저작일
- 2001.06
- 7페이지/ 어도비 PDF
- 가격 4,000원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국유화학회
ㆍ수록지정보 : 韓國油化學會誌 / 18권 / 2호
ㆍ저자명 : 김지현, 김희석, 임연수, 박홍수, 김명수
영어 초록
Due to its low density, good mechanical properties and chemical inertness, glassy carbon(GC) has been studied for appications in several fields. A raw thermosetting resin of furanic resin was polymerized with a curing agent of p-toluenesulfonic acid monohydrate. The maximum yield of GC was obtained at the curing agent content of 1.0 wt% in furanic resin. In order to make thick GC, the affect of graphite filler addition to the furanic resin was investigated. The density and electrical resitivity of GC after graphitization were 1.45 g/cm3 and 47 ×10-4 Ω · cm respectively and the amorphous structure of GC was confirmed by XRD profiles with very broad peaks comparable to those of graphite at 206˚ and 45˚.