전기선폭발법으로 제조된 텅스텐 분말의 산소 조성이 방전플라즈마소결 거동에 미치는 영향

서지정보

ㆍ발행기관 : 한국분말야금학회 ㆍ수록지정보 : 한국분말야금학회지 / 21권 / 6호
ㆍ저자명 : 김철희, 이성, 김병기, 김지순

영어 초록

Effect of oxygen content in the ultrafine tungsten powder fabricated by electrical explosion of wire method on the behvior of spark plasma sintering was investigated. The initial oxygen content of 6.5 wt% of as-fabricated tungsten powder was reduced to 2.3 and 0.7 wt% for the powders which were reduction-treated at 400˚C for 2 hour and at 500˚C for 1h in hydrogen atmosphere, respectively. The reduction-treated tungsten powders were spark-plasma sintered at 1200-1600˚C for 100-3600 sec. with applied pressure of 50 MPa under vacuum of 0.133 Pa. Maximun sindered density of 97% relative density was obtained under the condition of 1600˚C for 1h from the tungsten powder with 0.7 wt% oxygen. Sintering activation energy of 95.85kJ/mol-1 was obtained, which is remarkably smaller than the reported ones of 380~460kJ/mol-1 for pressureless sintering of micron-scale tungsten powders.