Preparation and thermal properties of polyethylene-based carbonized fibers
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국탄소학회
ㆍ수록지정보 : Carbon Letters / 16권 / 1호
ㆍ저자명 : Kwan-Woo Kim, Hye-min Lee, Byoung Suhk Kim, Seon-Hwan Hwang, Lee-Ku Kwac, Kay-Hyeok An and Byung-Joo Kim
ㆍ저자명 : Kwan-Woo Kim, Hye-min Lee, Byoung Suhk Kim, Seon-Hwan Hwang, Lee-Ku Kwac, Kay-Hyeok An and Byung-Joo Kim
목차
1. Introduction2. Experiment Details
3. Results and Discussion
4. Conclusion
Acknowledgments
References
한국어 초록
In this study, carbonized fibers were prepared by using acidically cross-linked LDPE fibers. The surface morphologies of the carbonized fibers were observed by SEM. The effects of cross-linking process temperatures were studied using thermal analyses such as DSC and TGA. The melting and heating enthalpy of the fibers decreased as the cross-linking temperature increased. The cross-linked fibers had a carbonization yield of over 50%. From SEM results the highest yield of carbonized LDPE-based fibers was obtained by cross-linking at a sulfate temperature (170oC). As a result, carbonation yield of the carbonized fibers was found to depend on the functions of the cross-linking ratio of the LDPE precursors.영어 초록
In this study, carbonized fibers were prepared by using acidically cross-linked LDPE fibers. The surface morphologies of the carbonized fibers were observed by SEM. The effects of cross-linking process temperatures were studied using thermal analyses such as DSC and TGA. The melting and heating enthalpy of the fibers decreased as the cross-linking temperature increased. The cross-linked fibers had a carbonization yield of over 50%. From SEM results the highest yield of carbonized LDPE-based fibers was obtained by cross-linking at a sulfate temperature (170oC). As a result, carbonation yield of the carbonized fibers was found to depend on the functions of the cross-linking ratio of the LDPE precursors.참고 자료
없음"Carbon Letters"의 다른 논문
- Influence of Nitrogen moieties on CO2 capture of Carbon..5페이지
- Conducting and interface characterization of carbonate-..6페이지
- CO2 adsorption characteristics of slit-pore shaped acti..6페이지
- Preparation of sulfonated reduced graphene oxide by rad..4페이지
- Effect of surface treatment of graphene nanoplatelets f..7페이지