Polyaniline–graphene quantum dots (PANI–GQDs) hybrid for plastic solar cell
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국탄소학회
ㆍ수록지정보 : Carbon letters / 30권 / 1호
ㆍ저자명 : Gebremedhin Gebremariam Gebreegziabher, Assefa Sergawie Asemahegne, Delele Worku Ayele, Dhakshnamoorthy Mani, Rewrewa Narzary, Partha Pratim Sahu, Ashok Kumar
ㆍ저자명 : Gebremedhin Gebremariam Gebreegziabher, Assefa Sergawie Asemahegne, Delele Worku Ayele, Dhakshnamoorthy Mani, Rewrewa Narzary, Partha Pratim Sahu, Ashok Kumar
목차
Abstract1 Introduction
2 Experimental methods
2.1 Chemicals
2.2 Materials’ synthesis
2.3 Characterization
2.4 Results and discussion
2.5 Efficiency
3 Conclusion
Compliance with ethical standards
References
영어 초록
Polyaniline–graphene quantum dots (PANI–GQDs) are considered as an important candidate for applications in photovoltaic cells. In this work, GQDs were prepared using sono-Fenton reagent from reduced graphene oxide (rGO). PANI–GQD hybrid was also synthesized using the chemical in situ polymerization method. The synthesized materials were characterized using UV–visible (UV–Vis) spectroscopy, photoluminescence (PL) spectroscopy, current–voltage (I–V) characteristic, thermal gravimetric analysis (TGA), Raman spectroscopy, and X-ray diffraction (XRD). Dynamic light scattering was also used to estimate the lateral size of GQDs. The enhanced visible-light absorbance in the hybrid was confirmed by UV–Vis analysis and the decrease in intensity around 3461 cm−1 in FT-IR spectra was due to the interaction between functional groups of PANI with GQDs. This led to improved thermal stability and conductivity as observed from TGA and I–V analysis, respectively. Moreover, the Raman spectrum for PANI–GQDs showed a decrease in the peak at ~ 1348 and ~ 1572 cm−1 as compared to PANI and GQDs. Similarly, from the XRD profile of PANI–GQDs, a shift in peak was observed due to an alteration in the microstructure. A sandwich device with cell structure glass/ITO/PANI–GQDs/Al was fabricated and its application was tested. Current density–voltage (J–V) curve of the device was measured with a Keithley SMU 2400 unit under an illumination intensity of 100 Wm−2 simulating the AM 1.5 solar spectrum. The hybrid exhibited photovoltaic properties, and 0.857% efficiency was observed in response to the applied voltage. This work suggests that PANI can be used as an alternative material for photovoltaic cells.참고 자료
없음"Carbon letters"의 다른 논문
- All‑solid‑state supercapacitor composed of reduced grap..7페이지
- Utilization of carbon dioxide onto activated carbon fib..7페이지
- Preparation and evaluation of surfactant‑stabilized gra..6페이지
- Microwave‑enhanced chemical vapor deposition graphene n..12페이지
- Electrochemical characterization of reduced graphene ox..8페이지
- In situ fabrication of high‑percent Ni–graphene nanocom..9페이지
- Electrochemical performances of semi‑transparent and st..7페이지
- Preparation of petroleum‑based mesophase pitch toward c..10페이지
- Preparation of graphene‑coated anodic alumina substrate..11페이지
- Chemical incorporation of epoxy‑modified graphene oxide..10페이지