염료감응형 태양전지용 코발트실리사이드들의 촉매 물성
(주)코리아스칼라
- 최초 등록일
- 2016.10.11
- 최종 저작일
- 2016.08
- 5페이지/ 어도비 PDF
- 가격 4,000원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국재료학회
ㆍ수록지정보 : 한국재료학회지 / 26권 / 8호
ㆍ저자명 : 김광배, 노윤영, 송오성
목차
1. 서 론
2. 실험 방법
3. 결과 및 고찰
4. 결 론
References
영어 초록
The cobalt silicides were investigated for employment as a catalytic layer for a DSSC. Using an E-gun evaporation process, we prepared a sample of 100 nm-thick cobalt on a p-type Si (100) wafer. To form cobalt silicides, the samples were annealed at temperatures of 300 oC, 500 oC, and 700 oC for 30 minutes in a vacuum. Four-point probe, XRD, FE-SEM, and CV analyses were used to determine the sheet resistance, phase, microstructure, and catalytic activity of the cobalt silicides. To confirm the corrosion stability, we also checked the microstructure change of the cobalt silicides after dipping into iodide electrolyte. Through the sheet resistance and XRD results, we determined that Co2Si, CoSi, and CoSi2 were formed successfully by annealing at 300 oC, 500 oC, and 700 oC, respectively. The microstructure analysis results showed that all the cobalt silicides were formed uniformly, and CoSi and CoSi2 layers were very stable even after dipping in the iodide electrolyte. The CV result showed that CoSi and CoSi2 exhibit catalytic activities 67 % and 54 % that of Pt. Our results for Co2Si, CoSi, and CoSi2 revealed that CoSi and CoSi2 could be employed as catalyst for a DSSC.
참고 자료
없음
"한국재료학회지"의 다른 논문
더보기 (4/9)