Electrical Properties and Microstructures in Ti Films Deposited by TFT dc Sputtering
(주)코리아스칼라
- 최초 등록일
- 2016.06.04
- 최종 저작일
- 2016.04
- 5페이지/ 어도비 PDF
- 가격 4,000원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국재료학회
ㆍ수록지정보 : 한국재료학회지 / 26권 / 4호
ㆍ저자명 : Chang-Suk Han, Seung-Jin Jeon
목차
1. Introduction
2. Experimental Procedure
3. Results
4. Discussion
5. Conclusion
Acknowledgements
References
영어 초록
Ti films were deposited on glass substrates under various preparation conditions in a chamber of two-facing-target type dc sputtering; after deposition, the electric resistivity values were measured using a conventional four-probe method. Crystallographic orientations and microstructures, including the texture and columnar structure, were also investigated for the Ti films. The morphological features, including the columnar structures and surface roughness, are well explained on the basis of Thornton’s zone model. The electric resistivity and the thermal coefficient of the resistivity vary with the sputtering gas pressure. The minimum value of resistivity was around 0.4 Pa for both the 0.5 μm and 3.0 μm thick films; the apparent tendencies are almost the same for the two films, with a small difference in resistivity because of the different film thicknesses. The films deposited at high gas pressures show higher resistivities. The maximum of TCR is also around 0.4 Pa, which is the same as that obtained from the relationship between the resistivity and the gas pressure. The lattice spacing also decreases with increasing sputtering gas pressure for both the 0.5 μm and 3.0 μm thick films. Because they are strongly related to the sputtering gas pressures for Ti films that have a crystallographic anisotropy that is different from cubic symmetry, these changes are well explained on the basis of the film microstructures. It is shown that resistivity measurement can serve as a promising monitor for microstructures in sputtered Ti films.
참고 자료
없음
"한국재료학회지"의 다른 논문
더보기 (4/9)