Simultaneous Synthesis and Consolidation of Nanostructured MoSi2-NbSi2 Composite by High-Frequency Induction Heated Sintering and Its Mechanical Properties
(주)코리아스칼라
- 최초 등록일
- 2016.04.02
- 최종 저작일
- 2014.04
- 6페이지/ 어도비 PDF
- 가격 4,000원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국재료학회
ㆍ수록지정보 : 한국재료학회지 / 24권 / 4호
ㆍ저자명 : Kang, Hyun-Su, Shon, In-Jin
영어 초록
The current concern about these materials (MoSi2 and NbSi2) focuses on their low fracture toughness below theductile-brittle transition temperature. To improve the mechanical properties of these materials, the fabrication of nanostructuredand composite materials has been found to be effective. Nanomaterials frequently possess high strength, high hardness, excellentductility and toughness, and more attention is being paid to their potential application. In this study, nanopowders of Mo, Nb,and Si were fabricated by high-energy ball milling. A dense nanostructured MoSi2-NbSi2 composite was simultaneouslysynthesized and sintered within two minutes by high-frequency induction heating method using mechanically activated powdersof Mo, Nb, and Si. The high-density MoSi2-NbSi2 composite was produced under simultaneous application of 80MPa pressureand an induced current. The sintering behavior, mechanical properties, and microstructure of the composite were investigated.The average hardness and fracture toughness values obtained were 1180kg/mm2 and 3MPa·m1/2, respectively. These fracturetoughness and hardness values of the nanostructured MoSi2-NbSi2 composite are higher than those of monolithic MoSi2 orNbSi2.
참고 자료
없음
"한국재료학회지"의 다른 논문
더보기 (1/6)