확산펌프 기반의 O2 축전결합 플라즈마를 이용한 PMMA와 폴리카보네이트의 건식 식각
(주)코리아스칼라
- 최초 등록일
- 2016.04.02
- 최종 저작일
- 2009.08
- 6페이지/ 어도비 PDF
- 가격 4,000원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국재료학회
ㆍ수록지정보 : 한국재료학회지 / 19권 / 8호
ㆍ저자명 : 박주홍, 이성현, 최경훈, 노호섭, 이제원
영어 초록
We report on the capacitively coupled O2 plasma etching of PMMA and polycarbonate (PC) with a diffusion pump. Plasma process variables were process pressure and CCP power at 5 sccm O2 gas flow rate. Characterization was done in order to analyze etch rate, etch selectivity, surface roughness, and morphology using stylus surface profilometry and scanning electron microscopy. Self bias decreased with increase of process pressure in the range of 25~180 mTorr. We found an important result for optimum pressure for the highest etch rate of PMMA and PC, which was 60 mTorr. PMMA and PC had etch rates of 0.46 and 0.28 μm/min under pressure conditions, respectively. More specifically, etch rates of the materials increased when the pressure changed from 25 mTorr to 60 mTorr. However, they reduced when the pressure increased further after 60 mTorr. RMS roughnesses of the etched surfaces were in the range of 2.2~2.9 nm. Etch selectivity of PMMA to a photoresist was ~1.5:1 and that of PC was ~0.9:1. Etch rate constant was about 0.04 μm/minW and 0.02 μm/minW for PMMA and PC, respectively, with the CCP power change at 5 sccm O2 and 40 mTorr process pressure. PC had more erosion on the etched sidewall than PMMA did. The OES data showed that the intensity of the oxygen atomic peak (777.196 nm) proportionally increased with the CCP power.
참고 자료
없음
"한국재료학회지"의 다른 논문
더보기 (4/9)