단결정 초내열합금에서 응고속도에 따른 응고 및 공정조직의 형성 거동
(주)코리아스칼라
- 최초 등록일
- 2016.04.02
- 최종 저작일
- 2008.11
- 6페이지/ 어도비 PDF
- 가격 4,000원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국재료학회
ㆍ수록지정보 : 한국재료학회지 / 18권 / 11호
ㆍ저자명 : 이재현
영어 초록
Directional solidification experiments were carried out at 1-300 μm/sec solidification rates in the single crystal superalloy, CMSX 10. The solid/liquid interface morphology changed from planar to dendritic, and the dendrite spacing became finer as the solidification rate increased. The pool size of the γ/γ' eutectic, formed between dendrites, reduced as the solidification rate increased. The phase formation temperatures, such as the solidus, liquidus and eutectic, were estimated by differential scanning calorimetry (DSC) analysis. The morphology of the γ/γ' phase, known to be eutectic, showed γ' cells with a γ intercellular network, and this γ/γ' was composed of coarse and fine γ/γ' regions. In this study, it is suggested that the γ/γ' phase was a coupled peritectic.The solidification procedure of the γ/γ' between dendrites is also discussed.
참고 자료
없음
"한국재료학회지"의 다른 논문
더보기 (4/9)