황산 환경에서 Fe-Si, Ni-Ti계 및 Ni 합금의 내부식성 특성
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국재료학회
ㆍ수록지정보 : 한국재료학회지 / 21권 / 1호
ㆍ저자명 : 권혁철, 김동진, 김홍표, 박지연, 홍성덕
ㆍ저자명 : 권혁철, 김동진, 김홍표, 박지연, 홍성덕
영어 초록
Methods of producing hydrogen include steam reforming, electrochemical decomposition of water, and the SI process. Among these methods, the Sulfur iodine process is one of the most promising processes for hydrogen production. The thermochemical sulfur-iodine (SI) process uses heat from a high-temperature-gas nuclear reactor to produce H2 gas; this process is known for its production of clean energy as it does not emit CO2 from water. But the SI-process takes place in an extremely corrosive environment for the materials. To endure SI environments, the materials for the SI environment will have to have strong corrosion resistance. This work studies the corrosion resistances of the Fe-Si, Ni-Ti and Ni Alloys, which are tested in SI-process environments. Among the SI-process environments, the conditions of boiling sulfuric acid and decomposed sulfuric acid are selected in this study. Before testing in boiling sulfuric acid environments, the specimens of Fe-4.5Si, Fe-6Si, Ni-4.5Si, Ni-Ti-Si-Nb and Ni-Ti-Si-Nb-B are previously given heat treatment at 1000˚C for 48 hrs. The reason for this heat treatment is that those specimens have a passive film on the surface. The specimens are immersed for 3~14 days in 98wt% boiling sulfuric acid. Corrosion rates are measured by using the weight change after immersion. The corrosion rates of the Fe-6Si and Ni-Ti-Si-Nb-B are found to decrease as the time passes. The corrosion rates of Fe-6si and Ni-Ti-Si-Nb-B are measured at 0.056 mm/yr and 0.16 mm/yr, respectively. Hastelloy-X, Alloy 617, Alloy 800H and Haynes 230 are tested in the decomposed sulfuric acid for one day. Alloy 800H was found to show the best corrosion resistance among the materials. The corrosion rate of Alloy 800H is measured at -0.35 mm/yr. In these results, the corrosion resistance of materials depends on the stability of the oxide film formed on the surface. After testing in boiling sulfuric acid and in decomposed sulfuric acid environments, the surfaces and compositions of specimens are analyzed by SEM and EDX.참고 자료
없음"한국재료학회지"의 다른 논문
- La이 도핑된 CuO-ZnO-Al2O3 복합 산화물의 합성공정개발5페이지
- 다중소스 진공증착법에서의 대면적 박막균일도에 관한 전산모사 연구11페이지
- 합금강관의 Energy Resistance Welding 용접조건에 따른 미세조직 거동 및 기계적 ..6페이지
- Bi를 첨가한 백색 LED용 ZnS:Mn 황색형광체의 발광특성4페이지
- Analysis of the Aluminum Extrusion Process Equipped wit..7페이지
- 버퍼막 두께에 따른 ZnO/ZnO/p-Si(111) 이종접합 다이오드 특성 평가5페이지
- Fe 입자를 미세 분산 시킨 AlN 박막의 물리적 성질6페이지
- 나노 구조를 가지는 다공성 주석 산화물의 전기화학적 특성7페이지
- 동속압연과 이속압연이 동합금판재의 조직 및 기계적 성질에 미치는 영향6페이지
- 폴리페닐카보실란을 이용한 SiOC가 코팅된 스테인리스스틸 제조 및 이의 내부식성 특징7페이지