우리는 TiO2_Cu 15%, TiO2_Cu 15%_Ag15%, TiO2_Cu 15%_Ag30%을 TiO2 Dye degradation 등의 과정을 거쳐 합성하여 시간에 따른 반응 ... Figure SEQ Figure \* ARABIC 6 TiO2 Dye degradation UV spectrum TiO2_Cu 15% Ag 15% 합성 2-1) 실험과정 바이알에 TiO2 ... 일반 TiO2와 결과값 비교 일반 TiO2의 흡광도 그래프는 위의 Figure 6과 같으며, 이 실험에서 합성한 TiO2_Cu15%, Ag15%의 흡광도 그래프는 위의 Figure
To improve photocatalytic performance, a PbS/ZnO/TiO2 nanotube catalyst was synthesized, and its surface ... The PbS/ZnO/TiO2 photocatalyst significantly enhanced the photocatalytic activity for dye degradation
To improve photocatalytic efficiency, graphene/Ag/TiO2 nanotube catalyst was synthesized, and its surface ... For deposition of Ag nanoparticles on the TiO2 nanotubes, a polymer compound containing CH3COOAg/poly ... Graphene deposition on the Ag/TiO2 nanotubes was achieved using an electrophoretic deposition process
Ni-TiO2 조합전극을 환원전극으로 그라파이트를 산화전극으로 사용하였으며, 셀전위를 제어하면서 TiO2의 전해환원 특성을 관찰하였다. ... 본 연구에서는 850℃의 CaCl2 용융염계에서 전해환원공정을 통해 TiO2로부터 금속티타늄을 제조하였 다. ... XRD 분석을 통해 TiO2가 CaTiO3, Ti2O, Ti6O와 같은 다양한 반응 중간생성물을 거쳐 Ti 스폰지로 환원되는 것이 밝혀졌다.
대표적인 예로는 산화타이타늄 TiO2이 있다. 광화학반응을 촉진시키는 물질을 말하며 반도체·색소·엽록소도 그 중 하나이다. ... 반도체의 산화타이타늄 TiO2에 의한 효과는 1967년 두 명의 일본인 과학자에 의해 증명되었고, 환경문제 해결에도 도움이 되는 기초기술로 실용화되기 시작하였다. ... 이 광촉매반응을 통하여 형성된 반응성물질(예, 이산화티탄늄(TiO2)에 빛을 조사면 결정표면에 생기는 전자가 이탈한 정공이 물 분자와 반응해서 산화력이 매우 큰 하이드록시 라디컬을
The results show that the TiO2- x-6 h, TiO2- x-24 h, and TiO2- x-48 h samples have the main product of ... Herein, TiO2- x nanostructures have been prepared by a simple solvothermal method and engineered by the ... oxygen vacancy signal gradually increases while the band gap becomes narrow for the as-synthesized TiO2
One-dimensional rutile TiO2 is an important inorganic compound with applicability in sensors, solar ... The formation of TiO2 nanowires is greatly influenced by synthesis temperature and pressure. ... In this work, we report the growth of TiO2 nanowires on a Ti alloy powder (Ti-6wt%Al- 4wt%V, Ti64) using
실험결과 정렬된 구조의 TiO2 층이 Al2O3 지지체에 형성되었다. TiO2 층 형성 후 제조된 세라믹 분리막의 순수 투과도는 형성된 광촉매 층 저항으로 감소하였다. ... 높은 공극률과 균질성을 지닌 TiO2 광촉매층을 그라프트 공중합체를 사용하여 제조하였다. ... 정렬된 구조의 TiO2 층은 UV 결합 시 5시간 안에 완벽한 염색용액 분해를 달성시킬 수 있었다.
PURPOSES : The purpose of this study was to evaluate the performance of a titanium dioxide (TiO2) asphalt ... METHODS : To verify the NOx reduction performance of TiO2 and silicon-based resin-applied surface treatment ... was verified using a full-scale demonstration facility, and the field construction capability of the TiO2
In this study, TiO2 powders are synthesized from ammonium hexafluoride titanate (AHFT, (NH4)2TiF6) as ... The ratio of anatase to rutile phase in TiO2 is estimated by XRD. ... Then, to prepare the TiO2 powders, is heat-treated at 300-1300oC for 1 h.
TiO2 nanotube was grown on Ti by anodic oxidation to create TiO2 nanotube plate which can be used as ... 본 연구에서는 TiO2 nanotube 광촉매의 고도산화처리능을 비교하기 위해서 OH 라디칼 생성 력을 평가하고자 하였다. ... 따른 Probe compound인 4-Chlorobenzoic acid (pCBA)의 농 도 감소에 따라 OH radical 생성량을 산정하는 방법으로 광촉매 효율을 평가하였는데, TiO2
A TiO2/CNT nanohybrid photocatalyst is synthesized via sol-gel route, with titanium (IV) isopropoxide ... The TiO2/CNT composite exhibits a fast grain growth and phase transformation during calcination. ... at 450oC, 550oC and 650oC in air are compared with those of pure TiO2 using field-emission scanning
of NH2– B–TiO2. ... In this work, selectively coupling Cu(OH)2 and CuO with amine-modified brookite TiO2 ( NH2–B–TiO2) has ... of a p–n junction between NH2– B–TiO2 and CuO interfaces, while in the NH2– B–TiO2–Cu(OH)2 composite
TiO2 용액 100 mL : TiO2 0.2 g 포함 ? 100 ppm MG 용액 25 mL ? 증류수 125 mL ? ... 실험 이론 산화타이타늄(TiO2)은 다양한 응용성을 띤 반도체이다. ... TiO_2 & +h nu &-> &e^- &+ &h^+ TiO2의 이러한 광촉매적인 역할은 태양열을 이용한 전기에너지의 생성, 광합성, 혹은 유해한 무기물질의 정화 등을 위해 응용할
The TiO2 coating fixation and dynamic pressure coating-type TiO2 fixation methods were used to solve ... The results showed that when the TiO2 coating fixation and dynamic pressure infiltration TiO2 fixation ... RESULTS : The long-term durability of the TiO2 coating fixation and dynamic pressure coating TiO2 fixation
그리고 TiO2의 첨가량이 증가할수록, 발광효율이 증가하는 것을 알 수 있었다. ... TiO2는 내산성, 내알칼리성이 좋아 인체에 무해하기 때문에 광촉매제로 많이사용되고 있다. ... Therefore TiO2 has been most often used in the photocatalyst.
Uniform TiO2 blocking layers (BLs) are fabricated using ultrasonic spray pyrolysis deposition (USPD) ... Therefore, optimized TiO2 BLs fabricated by USPD may allow performance improvements in DSSCs. ... Compared to the other samples, the DSSC containing the uniform TiO2 BL of 70 nm in thickness shows a
In this study, TiO2/TiOF2 heterostructured composite powders with suitable band structures, which structures ... This result shows that the TiO2/TiOF2 heterostructure promotes the separation of the photoinduced electrons ... The powder with a phase volume ratio close to 1, compared with single TiOF2 and other composite powders