Synthesis and characterization of microporous activated carbon from rubberwood by chemical activation with KOH
(주)코리아스칼라
- 최초 등록일
- 2023.05.08
- 최종 저작일
- 2021.10
- 10페이지/ 어도비 PDF
- 가격 4,000원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국탄소학회
ㆍ수록지정보 : Carbon letters / 31권 / 5호
ㆍ저자명 : Wasutha Thongpat, Juntakan Taweekun, Kittinan Maliwan
목차
Abstract
1 Introduction
2 Materials and methods
2.1 Material and preparation of rubberwood activated carbon
2.2 Characterization of rubberwood char and activated carbon
3 Results and discussion
3.1 The yield of rubberwood char and activated carbon
3.2 Proximate and ultimate analysis
3.3 Surface area and pore analysis
3.4 Adsorption isotherm
3.5 Field emission scanning electron microscope analysis
4 Conclusion
Acknowledgements
References
영어 초록
This research aims to study the effect of impregnation ratio and activation temperature on microporous development of activated carbon (AC). Rubberwood chips, which are wasted from home furnishing industry, were used as precursors for synthesized of activated carbon by chemical activation employing Potassium hydroxide (KOH) as activation agent. Rubberwood char was carbonized at 400 °C for 1 h under inert gas. In this experiment, the rubberwood chars were impregnated with KOH solution by 1:1–3 (char: KOH) impregnation ratio for 24 h, then the samples were activation at 600–800 °C. Surface area, pore volume, micropore volume, pore size distribution, adsorption isotherm and porous structure were analyzed in this experiment to identify the properties of derived activated carbon. According to the investigation, the activated carbon, activated at 800 °C with impregnation ratio of 1:3, demonstrated the highest surface area, pore volume and micropore volume as 1491.75 m2/g, 0.6777 cm3/g, and 0.5813 cm3/g, respectively. Its average pore size was 1.82 nm and it also showed type I adsorption isotherm which indicates as microporous solid.