Interpenetrating phase composites of -Cu system were produced via Spark-Plasma Sintering (SPS) oi nanocomposite powders. Under simultaneous action of..
기계적합금법으로 Ti와 B의 혼합분말로부터 TiB2분말을 제조하였고, Zr과 Ta의 Ti 치환 효과를 조사하였다. ... (Ti+B)의 혼합분말을 280시간 분쇄하여 TiB2단일상을 얻었고 기계적합금화 도중 비정질상은 관찰되지 않았다. ... Ti의 일부를 원자반경이 Ti보다 큰 Zr으로 치환한 결과 기계적합금화에 걸리는 시간이 크게 감소한 반면에, 붕화물 생성열이 절대값이 TiB2상보다 작은 Ta로 치환하면 280시간
A sintered body of TiB2-reinforced iron matrix composite (Fe-TiB2) is fabricated by pressureless-sintering ... Sintered compacts have two main phases of Fe and TiB2 along with traces of TiB, which seems to be formed ... that is intentionally added to complete the reaction for TiB2 formation.
/TiB2[010]//SiC[112], TiC(200)//TiB2(001)//SiC( 402 ) and TiC( 111 )//TiB2(101 )//SiC( 220 ). ... TiC-TiB2-SiC system was a ternary eutectic, whose eutectic composition was 34TiC-22TiB2-44SiC (mol%) ... TiC-TiB2-SiC ternary eutectic composite were synthesized by a floating zone method using TiC, TiB2 and
TiB2-reinforced iron matrix composite (Fe-TiB2) powder was in-situ fabricated from titanium hydride ... The results showed that TiB2 particles formed in nanoscale were uniformly distributed in Fe matrix. ... Fe2B phase existed due to an incomplete reaction of Ti and FeB.
AC2BS 무첨가 종횡비(사형) AC2BS 무첨가 종횡비(금형) AC2BS TiB첨가 종횡비(사형) AC2BS TiB첨가 종횡비(금형) AC2BS TiB+Sr첨가 종횡비(사형) AC2BS ... TiB 및 Sr첨가에 따른 AC2BS 냉각곡선그래프 Table. 3.2.1. TiB 및 Sr첨가에 따른 AC2BS 초정 및 공정 구상화가 다수 진행 된것도 확인이 된다. ... 2.2.1 Density Index 측정7 2.2.2 냉각곡선 분석7 2.2.3 조직 관찰8 3장 실험결과 및 고찰9 3.1 Density Index 측정9 3.2 TiB 및 Sr