Co, Ni 농도 변화에 따른 나노 SnO2 센서의 감응 특성
(주)코리아스칼라
- 최초 등록일
- 2016.04.02
- 최종 저작일
- 2011.10
- 4페이지/ 어도비 PDF
- 가격 3,000원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국재료학회
ㆍ수록지정보 : 한국재료학회지 / 21권 / 10호
ㆍ저자명 : 이지영, 유윤식, 유일
영어 초록
Nano-sized SnO2 thick films were prepared by a screen-printing method onto Al2O3 substrates. The sensing characteristics were investigated by measuring the electrical resistance of each sensor in a test box as a function of the detection gas. The nano-sized SnO2 thick film sensors were treated in a N2 atmosphere. The structural properties of the nano SnO2with a rutile structure according to XRD showed a (110) dominant SnO2 peak. The particle size of SnO2:Ni nano powders at Ni 8 wt% was about 45 nm, and the SnO2 particles were found to contain many pores according to the SEM analysis. The sensitivity of the nano SnO2-based sensors was measured for 5 ppm CH4 gas and CH3CH2CH3 gas at room temperature by comparing the resistance in air with that in the target gases. The results showed that the best sensitivity of SnO2:Ni and SnO2:Co sensors for CH4 gas and CH3CH2CH3 gas at room temperature was observed in SnO2:Ni sensors doped with 8 wt% Ni. The response time of the SnO2:Ni gas sensors was 10 seconds and recovery time was 15 seconds for the CH4 and CH3CH2CH3 gases.
참고 자료
없음
"한국재료학회지"의 다른 논문
더보기 (3/8)