롤투롤시스템을 이용하여 PET 필름위에 제조된 SiO2-ITO 박막의 색도(b*), 면저항과 투과도 연구

서지정보

ㆍ발행기관 : 한국재료학회 ㆍ수록지정보 : 한국재료학회지 / 21권 / 5호
ㆍ저자명 : 박미영, 김정수, 강보갑, 김혜영, 김후식, 임우택, 최식영

영어 초록

This paper has relatively high technical standard and experimental skill. The fabrication of TCO film with hightransparency, low resistance and low chromaticity require exact control of several competing factors. This paper has resolvedthese problems reasonably well, thus recommended for publication. Indium tin oxide(ITO) thin films were by D.C. magnetronroll-to-roll sputter system utilizing ITO and SiO2 targets of ITO and SiO2. In this experiment, the effect of D.C. power, windingspeed, and oxygen flow rate on electrical and optical properties of ITO thin films were investigated from the view point ofsheet resistance, transmittance, and chromaticity(b*). The deposition of SiO2 was performed with RF power of 400W, Ar gasof 50sccm and the deposition of ITO, DC power of 600W, Ar gas of 50sccm, O2 gas of 0.2sccm, and winding speed of 0.56m/min. High quality ITO thin films without SiO2 layer had chromaticity of 2.87, sheet resistivity of 400ohm/square, and trans-mittance of 88% and SiO2-doped ITO Thin film with chromaticity of 2.01, sheet resistivity of 709ohm/square, and transmittanceof more than 90% were obtained. As a result, SiO2 was coated on PET before deposition of ITO, their chromaticity(b*) andtransmittance were better than previous results of ITO films. These results show that coating of SiO2 induced arisingchromaticity(b*) and transmittance. If the thickness of SiO2 is controlled, sheet resistance value of ITO film will be expected tobe better for touch screen. A four point probe and spectrophotometer are used to investigate the properties of ITO thin films.

참고 자료

없음