인과 염소 함유 변성폴리에스테르의 PU 난연도료에의 적용
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국유화학회
ㆍ수록지정보 : 韓國油化學會誌 / 24권 / 1호
ㆍ저자명 : 박홍수, 김송형, 홍석영, 유규열, 안성환, 함현식, 김승진, 김영근
ㆍ저자명 : 박홍수, 김송형, 홍석영, 유규열, 안성환, 함현식, 김승진, 김영근
영어 초록
This study was focused on the maximization of flame-retardancy of polyesters by a synergism of simultaneously introduced chlorine and phosphorus into polymer chains of modified polyesters. To prepare modified polyesters, reaction intermediates, TD-adduct (prepared from trimethylolpropane/2,4-dichlorobenzoic acid (2,4-DCBA)) and TMBO (prepared from tetramethylene bis(orthophosphate)), were prepared first, then condensation polymerization of the prepared intermediates, adipic acid, and 1,4-butanediol were carried out. In the condensation polymerization, the content of phosphorus was fixed to be 2%, and the content of 2,4-DCBA that provides chlorine component was varied to be 10, 20, and 30wt%, and we designated the prepared modified polyesters containing chlorine and phosphorus as ABTT-10C, -20C, -30C. Two-component PU flame-retardant coatings (ABTTC, ABTTC-10C, ABTTC-20C, ABTTC-30C) were prepared by the curing of synthesized ABTTs with a curing agent of allophanate/trimer at room temperature. To examine the film properties of the prepared PU flame-retardant coatings, film specimens were prepared with the prepared coatings. The film properties of ABTTC, ABTTC-10C and ABTTC-20C, which contain 0, 10 and 20wt% 2,4-DCBA, respectively, were proved to be good, whereas the film properties of ABTTC-30C, which contains 30wt% 2,4-DCBA, was proved to be a little bit poor. Two kinds of flame retardancy tests, ˚45Meckel burner method and LOI method were performed. With the ˚45Meckel burner method, three flame-retardant coatings except ABTTC showed less than 3.4cm of char length, and showed less than 2 seconds of afterflaming and afterglow. From this result, the prepared flame-retardant coatings were proved to have the 1st grade flame retardancy. With the LOI method, the LOI values of the coatings containing more than 10wt% 2,4-DCBA were higher than 30%, which means that the coatings possess good flame retardancy. From these results, it was found that synergistic effect in flame retardancy was taken place by the introduced phosphorus and chlorine.참고 자료
없음"韓國油化學會誌"의 다른 논문
- 새로운 청색의 인광 물질을 어용한 유기 발광 소자의 전기적 특성 및 수명에 대한 연구5페이지
- 페롭스카이트 촉매의 제조와 메탄 산화에 응용7페이지
- 아날로그에 효과에 의한 토끼 근육 막 수축의 중간단계 연구6페이지
- Investigation of Top-Contact Organic Field Effect Trans..7페이지
- 펜톤산화에 의한 acenaphthene 또는 acenaphthylene 분해특성7페이지
- Resorcinol-formaldehyde resin와 고무 latex에 의해 표면 개질된 Kevl..8페이지
- 실란 변성아크릴수지의 합성과 고내후성 실리콘/아크릴수지 도료의 도막물성13페이지
- 산소 결함형 TiO2 분말의 가시광에 대한 광촉매 활성9페이지
- 무기흡착제를 이용한 CO2의 상온흡착6페이지
- 에탄올과 가솔린 혼합상에 대한 상분리 현상6페이지