영어 초록
In order to obtain the maximum flame retardancy with the minimal deterioration of physical properties of PU flame-retardant coatings, chlorine and phosphorous functional groups were introduced into the pre-polymer of modified polyesters. In the first step, the tetramethylene bis(orthophosphate) (TBOP) and neohexanediol dichloroacetate (DCA-adduct) intermediates were synthesized. In the second step, 1,4-butanediol and adipic acid monomers were polymerized with the two kind of intermediates to obtain copolymer. The modified polyesters containing chlorine and phosphorous (ATBA-10C, -20C, and -30C) were synthesized by adjusting the contents of chlorine compound (dichloroacetic acid, 10, 20, 30 wt%) with fixed the content of phosphorous compound (2 wt%). The PU flame-retardant coatings (TTBAH -10C, -20C, and -30C) were prepared using the synthesized ATBAs and HDI-trimer as curing agent at room temperature. The physical properties of PU flame-retardant coatings with chlorine and phosphorous were inferior to those with phosphorous only and the properties were getting worse with increasing chlorine content. Flame retardancy was tested with three methods. With the vertical method, Complete combustion time of ATBAHs were 259~347 seconds, which means that the prepared coatings are good flame-retardant. With the 45˚ Meckel burner method, char lengths of the three prepared coatings were less than 2.9 cm, which indicates that the prepared coatings are 1st grade flame retardancy. With the limiting oxygen index (LOI) method, the LOI values of the three prepared coatings were in the range of 30~35%, which proves good flame retardancy of the prepared coatings. From the results of flame retardancy tests of the specimens that contain the same amounts of flame retarding compounds, it was found that the coatings containing both phosphorous and chlorine show higher flame retardancy than the coatings containing phosphorous alone. This indicates that some synergy effect of flame retardancy exists between phosphorous and chlorine.참고 자료
없음"韓國油化學會誌"의 다른 논문
- 카프로락톤기 함유 90% 고형분인 아크릴수지의 하이솔리드 도료에의 적용11페이지
- 나노 실리카 하이브리드 박막의 산소 투과 특성8페이지
- 실리콘 코팅을 이용한 poly(ethylene naphthalate) 고온용 방열 필름의 제조7페이지
- 대칭적 Triazine 유도체들에 의한 중성 유제층의 경막시험에 관한 연구6페이지
- 브로일러에 대한 감마리놀렌산의 급원으로써 달맞이꽃종자유와 삼씨유;닭 껍질, 다리살 및 가슴살 지질의..9페이지
- 알칼리 촉매에 의한 우지(Beef Tallow)와 그 혼합지방의 Biodiesel화6페이지
- 인계화합물을 포함한 재활용 폴리우레탄폼의 난연성8페이지
- 유변학적 특성과 표면장력측정을 통한 음이온성 폴리머와 비이온성 계면활성제의 상호작용에 대한 연구7페이지
- 파라디옥사논의 고순도 정제를 위한 발한(sweating) 공정에 관한 연구9페이지
- Clofibrate의 연고기재에 의한 피부투과 특성7페이지