분무주조에 의해 제조된 Cu-Sn계 합금의 미세조직 및 인장성질

서지정보

ㆍ발행기관 : 한국분말야금학회 ㆍ수록지정보 : 한국분말야금학회지 / 17권 / 6호
ㆍ저자명 : 심상현, 강희수, 백경호

영어 초록

Cu-Sn based alloys were manufactured by gas atomization spray casting route in order to achieve a fine scale microstructure and a high tensile strength. The spray cast Cu-10Sn-2Ni-0.2Si alloy had an equiaxed grain microstructure, with no formation of brittle phase. Aging treatment promoted the precipitation of finely distributed particles corresponding to intermetallic phase throughout the -(CuSn) matrix. The cold-rolled Cu-Sn-Ni-Si alloy had a very high tensile strength of 1200 MPa and an elongation of 5%. Subsequent aging treatment at for 1h slightly reduced the tensile strength to 700 MPa and remarkably increased the elongation up to 30%. This result has been explained by coarsening the precipitates due to over aging and reducing the dislocation density due to annealing effects.