화학기상응축(Chemical Vapor Condensation)공정으로 제조한 L10규칙상 Fe50Pt50 나노분말의 특성

서지정보

ㆍ발행기관 : 한국분말야금학회 ㆍ수록지정보 : 한국분말야금학회지 / 14권 / 5호
ㆍ저자명 : 이경모, 유지훈, 이동원, 김병기, 김혁돈, 장태석

영어 초록

Ordered to FePt nanoparticles are strong candidates for high density magnetic data storage media because the phase FePt has a very high magnetocrystalline anisotropy , high coercivity and chemical stability. In this study, the ordered FePt nanoparticles were successfully fabricated by chemical vapor condensation process without a post-annealing process which causes severe particle growth and agglomeration. The nanopowder was obtained when the mixing ratio of Fe(acac) and Pt(arac) was 2.5 : 1. And the synthesized FePt nanoparticles were very fine and spherical shape with a narrow size distribution. The average particle size of the powder tended to increase from 5 nm to 10 nm with increasing reaction temperature from to . Characterisitcs of FePt nanopowder were investigated in terms of process parameters and microstructures.