Developing Hollow Carbon Balls by Oxidation of Carbon Blacks
(주)학지사
- 최초 등록일
- 2015.03.25
- 최종 저작일
- 2013.03
- 3페이지/ 어도비 PDF
- 가격 1,500원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국탄소학회
ㆍ수록지정보 : Carbon Letters / 14권 / 1호
ㆍ저자명 : Dong-SuKang, Beom-JunKim, Kwang-JuLee, Suk-HwanKim, Sang-WooLeeandJae-SeungRoh
목차
1. Introduction
2. Experimental Procedure
3. Results and Discussion
3.1. SSA and structural parameter
3.2. Microstructures
4. Conclusions
Acknowledgements
영어 초록
studied. Super P (SP) and Denka Black (DB) were used for this study. Specific surface area
(SSA), structural parameters, and microstructures were examined using Brunauer, Emmett
and Teller apparatus, X-ray diffraction spectroscopy, and transmission electron microscope
(TEM), respectively. The SSAs of both oxidized carbon blacks increased after oxidation.
The SSAs of raw DB and SP were 73 m2/g and 60 m2/g, respectively. Maximum SSAs
of oxidized DB and SP were 152 m2/g and 253 m2/g, respectively. The d002 of DB and SP
showed almost no change after oxidation. The Lc of raw DB (38 ) and SP (19 ) increased
with increasing weight loss. The Lc of SP increased up to 254 at 96% weight loss. The
SSA increased about twice in DB (148 m2/g) and about four times in SP (254 m2/g) after 3
h oxidation compared with the original carbon blacks. Through TEM observation the outer
parts of the oxidized carbon blacks showed a rigid shell structure and the inner parts looked
empty. Generally it looked like an angular soccer ball, so we named it ‘hollow carbon ball.’
It is expected that the hollow carbon ball can be used as catalyst supports.