The flameretardancy of RPUF was significantly enhanced by the incorporation of IPDI-GO, as evidenced ... This study underscores the potential of IPDI-GO as a promising flame retardant additive for RPUF. ... retardancy of rigid polyurethane foam (RPUF).
The study on the thermal and flame-retardant properties of the composites show that the modified [Dmim ... ]Es–graphene nanosheets improved the flameretardancy, smoke suppression and thermal stability of epoxy ... This work provides novel flame-retardant and graphene dispersion methods that broaden the range of applications
Theses new flame retardant coatings showed various properties comparable to other non flame retardant ... Two component polyurethane (PU) flame retardant coatings were prepared by blending trichloro modified ... TCMPs were synthesized by polycondensation of trichlorobenzoic acid (TCBA), a flame retardant component
There new flame-retardant coatings showed various properties comparable to other non-flame-retardant ... Coatings with 30wt% monochloroacetic acid was not flammable by the vertical flameretardancy test.
As a result, first, after flame time was measured at 0 seconds regardless of whether the flame retardant ... retardant treatments that show high flame retardant performance according to the botanical characteristics ... The purpose of this study is to compare and analyze the flame retardant performance of Japanese cypress
retardant. the flameretardance of synthesized flame retardant was proved with limiting oxygen index ... The structure of synthesized flame retardants was accomplished using FT-IR and 1H-NMR. ... halogen-free phosphoramidic flame retardant for polyurethane was synthesized with neopentyl glycol,
2 plant growth retardents (PGR), and growth response like plant height and leaf shape were evaluated ... height, but inflorescence elongation and flowering were inhibited greately as treated with plant growth retardants ... Flame), 적귀성 (Crassula capitella), 부용(Echeveria Pulv-oliver)을 대상으 로 생장억제제를 처리하여 초장이 짧고 관상가치가 높은 분 화의 생산이
Also, ETFE does not ensure the fire retardant performance, but this membrane material has the flame retardant ... this membrane material has the flame retardant performance of a thick fabric. ... to propose the fire and flame retardant performance criteria of membrane materials.
From the results of flameretardancy tests of the specimens that contain the same amounts of flameretarding ... Flameretardancy was tested with three methods. ... In order to obtain the maximum flameretardancy with the minimal deterioration of physical properties
There was no discernable difference in flame-retardancy between the two flame-retardant coatings, TBAOL ... Physical properties of the prepared flame-retardant coatings were tested. ... was in a range of 29~30%, which indicates that the two coatings are good flame-retardant coatings.
retarding component, respectively, showed the first grade flameretardancy with 2.8~3.9 cm of char length ... Flameretardancy was tested by a 45˚ Meckel burner method and LOI method. ... The flame-retardant coatings were prepared by blending the synthesized triphosphorus modified polyester
These results indicate that the coatings prepared in this study is good flame retardant one. ... Comparing the physical properties of the films of PIPUC with the film of non-flame retardant coatings ... , there was no degradation observed in physical properties by the introduction of a flame-retarding component
Most of the physical properties of the flame-retardant coatings were comparable to those of non-flame-retardant ... Two-component PU flame-retardant coatings (TATBCs) were prepared by blending TATBs with HDI-Biuret. ... containing 10 and 15wt% 1,4-butanediol, TATBC-10C and TATBC-15C were not flammable in the vertical flame-retardancy
To maximize a synergy effect in flame-retardancy of flame-retardant coatings, phosphorus and chlorine ... From this result, the prepared flame-retardant coatings were proved to have the 1st grade flameretardancy ... Two kinds of flameretardancy tests, 45˚Meckel burner method and LOI method, were performed.
From this result, the prepared flame-retardant coatings were proved to have the 1st grade flameretardancy ... Two kinds of flameretardancy tests, ˚45Meckel burner method and LOI method were performed. ... This study was focused on the maximization of flame-retardancy of polyesters by a synergism of simultaneously
Flameretardancy of the coatings was tested. ... PU flame-retardant coatings (APHD) containing phosphorous were prepared by blending of hexamethylene ... Moreover, the amount of afterglow and flameretardancy of the coatings are decreased with increasing
In order to obtain the maximum flameretardancy as well as the minimum deterioration of physical properties ... of PU flame-retardant coatings, chlorine and phosphorus functional groups were introduced into the pre-polymer ... of ATBAs were decreased with increasing DCA content because of the increase in hydroxyl group that retards
Since the retardancy of flame-retardant coatings containing chlorine and phosphorus groups was better ... In this study, two-component flame-retardant polyurethane coatings (TTBA-10C/HDI-trimer=TTHD-10C, TTBA ... The physical properties of the flame-retardant coatings containing chlorine and phosphorus groups were