The experimental results show that super-carburizing heat treatment gives rise to carbide dispersion ... across wider range of depth and higher carbon concentration than general carburizing heat treatment. ... after super-carburizing in order to improve the wear resistance of gear.
), 염욕 침탄(Salt bath carburizing), 가스 침탄(Gas carburizing), 플라즈마 침탄(Plasma carburizing), 진공 침탄(Vaccum carburizing ... 칭에 의해 표면층이 경화된다. (2) 전체가열 표면경화 열처리 ① 침탄(Carburizing) - 부품표면에 탄소의 확산침투에 의한 표면경화이다. - 예) 고체 침탄(Solid carburizing ... R E P O R T 제목 - 열처리 조사 학 과 신소재공학과 과 목 재료조직실험 목 차 ▶ 열처리 정의 ▶ 열처리 목적 ▶ 금속 열처리 종류와 방법 1. 일반 열처리 2.
Titanium carbide (TiC) powders are successfully synthesized by carburization of titanium hydride (TiH2 ... The mixtures are then heat-treated in an Ar atmosphere at 800-1200oC for carburization to occur. ... been experimentally and thermodynamically determined that the dehydrogenation, “TiH2 = Ti + H2”, and carburization
When the carbon concentration depth profile of the carburized specimen was measured for a short carburizing ... The carbon concentration in the carburized steels was measured by electron probe microanalysis (EPMA ... ) for a range of soluted carbon content in austenite from 0.1 to 1.2 wt%.
예를 들어 탄소 함유량이 적은 합금인 저탄소강, 저 Ni-Cr강, 저 Ni강 등의 금속과 침탄제(carburizer, carburizing reagent)를 혼합한 후 고온(850∼ ... 구상화의 방법에는 다소 높은 온도로 가열한 후 서서히 냉각시키는 방법, 1차 결정화 온도보다 20∼30℃ 낮은 온도에서 장시간에 거쳐 어닐링하는 방법, 1차 결정화 온도보다 20∼30 ... 열처리 어닐링과 노멀라이징에 대해 열처리 어닐링과 노멀라이징에 대해 열처리 - 어닐링 - 목 차 - 1. 열처리 1) 열처리의 개념 2) 열처리의 종류 3) 열처리의 역사 2.
주조와 가공에 의한 조직의 불균일 및 내부응력을 감소시키기 위한 조작으로 담금질의 가열온도보다 약간 높게 가열한 다음 공기 중에서 냉각하여 처리하는 방법. 2)표면 경화법 ㈎침탄법(carburizing ... 철금속 재료함유량이 0.1~0.3%이며 안전결선용 철사, 케이블 부싱, 나사 로드 등에 사용하며 판재로는 2차구조재로 사용한다. ... 1점 편집구성도(서론, 본론, 결론 구성) 1점 -1점 점 주제 적합성 1점 -1점 내용 충실도 1점 -1점 결론 및 참고자료(유무에 따라) 1점 -1점 아세아항공 직업전문학교 목 차
A method is developed to simulate the fatigue crack growth in a carburized gear tooth considering the ... The crack growth of carburized gears is measured by a crack gauge, and the validity of the simulation ... which corresponds to the fatigue strength is introduced in the method, and a new design procedure of carburized
This paper presents test results that demonstrate that vacuum carburizing system VacCarb™ carburized ... This approach is different from traditional carburizing methods, because vacuum carburizing is a non-equilibrium ... to faster carburization from within the pores.
현재 자동차용 소재 및 기계부품에 폭넓게 이용되는 SCM415강의 플라즈마 침탄 특성을 연구하기 위해 가스조성, 압력, 전류밀도, 온도 및 시간을 변수로 사용하였다. ... The influence of plasma carburizing process on the surface hardness of SCM415 low-alloy steel (0.15% ... case depth was proportional to the square root of carburizing time under the same current density.
The method used currently for the measurement of the carburization of the tubes is confirmed; carburizing ... increased and that the coarsening of Cr-carbide generated as a degree of carburization increased. ... The volume fraction of the carbide increased as the measuring point moved into the carburized side; this
Carbon content of CVC powder controlled by the gas phase carburization at 85 was well matched with the ... During the gas phase carburization, the particle size of WC increased from 20 nm to 40 nm and the long ... The sub-stochiometric CVC WC and WC-Co powders were carburized using the mixture gas of CH-H in the temperature
The reduction/carburization time decreased with increasing temperatures and carbon additions. ... The average size of WC particle carburized at by TEM was smaller than 50 nm. ... The oxide powder was mixed with carbon black by ball milling and this mixture was heated with various
Molybdenum and tungsten as active filler were carburized completely to , and WC in atmosphere. ... Hardness was increased with increasing carburization and reached 8.6-9.5 GPa in the specimen pyrolyzed
침탄(carburizing)은 가장 널리 사용되고 있는 표면 경화법이다. 침탄이란 재료의 표면만을 단단한 재질로 만들기 위해 다음과 같은 단계를 사용하는 방법이다. ... 20-30 20-25 15-25 40-50 10-20 40-50 20-30 5-10 800-900 800-900 800-900 850-900 치차, 적은 물건의 축, cam축, 자동차부품 ... 게이지류, 기계 및 공구부품 보통의 침탄제 저농도 17-23 8-12 15-40 45-55 20-30 5-15 6-20 850-900 900-930 크래크샤프트, 치차, 기계부품, 자동차부품