Ti 합금의 용체화열처리와 시효열처리에 따른 부식거동 Contents 서론 열처리 및 시험방법 실험 결과 및 고찰 서론 서론 저희 조는 바닷물에 장시간 노출되어 부식되거나 변질되지 ... 600°C 650°C 1 시간 4 시간 8 시간 16 시간 열처리 및 시험방법 Ti 합금의 성분 및 경도 열처리 온도 및 시간 전기화학적 분극곡선 실험 경도시험 열처리 및 시험방법 ... TI 선정 이유 서론 용체화 열처리 , 열처리에 따른 전기화학적 부식거동 연구 1066°C 966°C Ti ( 티타늄 ) : 내화 확성이 매우 강한 금속 , 내식성 우수 550°C
본 연구에서는 Ti에 Al 및 V등을 첨가한 α+β계에 대하여 1066℃와 966℃에서 5시간 용체화 열처리를 실시하고, 이 시편을 550℃, 600℃, 및 650℃에서 각각 1시간 ... In this study, the Ti alloys were solution heat treatment 5hours at 1066℃ and 966℃, and followed by aging
The addition of the Ti in Al-Li alloy promoted the formation of δ' phase. ... The addition of Ti on the δ' solvus line had a little effect over the thermodynamics δ' solvus line. ... In order to develop these purposed, the precipitation behaviors of the rapidly solidified Al-Li-Ti alloys
Herein, pre-forms of Ti-Al-xMn powder alloys are fabricated by compression forming. ... As intermetallic compounds based on Ti, TiAl alloys are becoming increasingly popular in the aerospace ... In this process, Ti powder is added to Al and Mn powders and compressed, and the resulting mixture is
The effect of Cr/Ti/Al elements in the alloy on high temperature oxidation was investigated using an ... A high-Cr/high-Ti oxide layer was formed on the blade surface under the heat-treated state considered ... temperature oxidation formed on the thermally exposed blade surface consisted of the following steps: ① Ti-oxide
In this study, Si3N4 / Ti5Si3 + TiN / TiN / Ti diffusing pairs were formed in the Si3N4 / Ti interfacial ... In addition, Ti and TiAl alloys are metals used in a variety of high temperature environments, and have ... Therefore, study of the interface reaction between Si3N4 / Ti and Si3N4 / TiAl can be a useful practice
/TiFe + β- Ti/BiIn containing phase). ... The microstructural evolution and modulation of mechanical properties were investigated for a Ti65Fe35 ... In particular, the primary dendrite phase changed from a TiFe intermetallic compound into a β-Ti solid
Although the Ti–6Al–4V alloy has been used in the aircraft industry owing to its excellent mechanical ... to investigate the effect of bulk shape on the microstructure and mechanical properties of L-PBFed Ti
It was concluded that this experimental approach can predict diverse welding conditions for Ti-6Al-4V ... In this study, fiber laser welding was conducted on 8.0mm thick Ti-6Al-4V alloy using the Bead On Plate
Stable phases of precipitates in the Al-Ti-Si and the Al-Ti-Zr alloys were identified as DO22- and each ... Rapidly solidified and mechanically alloyed Al-Ti base alloys were prepared by gas atomization and attritor ... Among the alloys, the mechanically alloyed Al-l0Ti-2Si alloy showed superior thermal stability and mechanical
기계적합금화한 Al-8wt.%(Ti+Zr)합금의 열적안정성에 미치는 Zr첨가의 영향에 대하여 조사하였다. ... Ti에 대한 Zr의 첨가비가 증가함에 따라 고온에서 장시간 노출에 따른 합금의 경도감소가 저하되어 합금의 열적안정성이 향상된 결과를 나타내었는데 이는 TEM 관찰결과 분산입자의 조대화가 ... XRD, SAD 및 EDS 분석결과 이러한 분산입자들은 DO2+와 DO23구조를 갖는 Al3(Ti+Zr)삼원계 금속간화합물이었으며 특히 DO23Al3(Ti+Zr)은 Zr의 첨가비가
기계적합금화 한 AI-Ti합금의 상온 및 고온 인장강도는 25at.% Ti을 Ce으로 치환함에 따라 증가하였다. ... 이는 Ce이 적은 고용도 효과에 의해 금속간화합물의 초대화를 억제하여 합금의 강도를 증가시키지만 다량 첨가시에는 Ti에 비해 무거운 원자량으로 인해 분산상의 부피분율을 감소시켜 합금의 ... %(Ti+Ce)합금의 변형에 필요한 활성화에너지는 AI의 자기확산에 필요한 에너지 (142kJ/mode)의 1.3-1.9배로 나타났다.
Ai-8wt.5(Ti+Zr)합금을 기계적합금화와 열간압출로 제조하여 Ti에 대한 Zr 첨가비와 등온열처리가 고온인장강도 및 변형거동에 미치는 영향에 대하여 조사하였다. ... AI-Ti-Zr 합금의 변형에 필요한 활성화에너지는 순수한 AI 기지의 자기확산에 필요한 활성화에너지 142KJ/mol에 비해 573-783K 온도범위에서 1.5-1.8배 높은 값을 ... 합금의 연성은 Zr 첨가량과 등온열처리에 관계없이 10% 이하로 낮게 나타났으며 인장 시험 온도가 고온일수록 취성파괴인 입계파괴가 지배적으로 일어났다.