Al-Zn 혼합물의 열 증발을 이용한 ZnO 결정의 합성에서 결정의 형상에 미치는 합성 온도와 시간의 영향
(주)코리아스칼라
- 최초 등록일
- 2016.04.02
- 최종 저작일
- 2015.06
- 4페이지/ 어도비 PDF
- 가격 3,000원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국재료학회
ㆍ수록지정보 : 한국재료학회지 / 25권 / 6호
ㆍ저자명 : 김민성
영어 초록
ZnO micro/nanocrystals at large scale were synthesized through the thermal evaporation of Al-Zn mixtures under air atmosphere. The effect of synthetic temperature and time on the morphology of the micro/nanocrystals was examined. It was found that the temperature and time affected the morphology of the ZnO crystals. At temperatures below 900 oC, no crystals were synthesized. At a temperature of 1000 oC, ZnO crystals with a rod shape were synthesized. With an increase in temperature from 1000 oC to 1100 oC, the morphology of the crystals changed from rod shape to wire and granular shapes. As the time increased from 2 h to 3 h at 1000 oC, tetrapod-shaped ZnO crystals started to form. XRD patterns showed that the ZnO crystals had a hexagonal wurtzite structure. EDX analysis revealed that the ZnO crystals had high purity. It is believed that the ZnO nanowires were grown via a vapor-solid mechanism because no catalyst particles were observed at the tips of the micro/nanocrystals in the SEM images.
참고 자료
없음
"한국재료학회지"의 다른 논문
더보기 (2/7)