열전대 시험

소개글

열전대에 관한 실험 레포트 입니다.

목차

Ⅰ. 서론 ················································································ 1
1.1. 연구배경 및 목적································································ 1
1.2 고온로란······························································· 1
1.3 열전대의 기본 원리와 정의······················································ 1
1.4 열전대의 상용온도 및 최대사용 온도표········································· 5
1.5 냉각곡선(Cooling Curve)·························································· 5
1.6 열전대의 종류 및 특성·························································· 6
1.7 각종 열전대의 온도, 열기전력 특성········································· 6

Ⅱ. 본론 ··············································································· 14
2.1 실험장치 ································································· 14
2.2 실험방법···································································· 16
2.3 실험측정값······································································16

Ⅲ. 결과 및 고찰 ································································· 18
3.1 Al의 냉각곡선························································· 18
3.2 Pb-wt19%Sn 실험 후 상태도제작·································19
3.3 고 찰············································································ 20

Ⅳ 참고문헌········································································ 20

본문내용

1.1 연구배경 및 목적
재료기초실험에서는 고온로를 많이 다루게 되므로, 노의 적절한 상요법과 정확한 온도 측정법을 익혀 두어야 한다. 본 실험에서는 실험실에서 열전대의 원리, 종류 및 특성과 그 사용방법을 익히도록 한다.

1.2 고온로란
공업적으로는 가스, 유류, 석탄 등을 연료로 하는 로와 전기를 이용한 고주파 및 저주파로, 저항로, arc로 등을 사용하고 있으나, 실험실용으로는 취급과 조절이 간편한 전기로가 많이 쓰이고 있다. 실험실용의 로는 그 형태에 따라 Muffle로, 관상로(tube furnace), 도나니로(crucible-furnace)등 3종으로 대별하며, 전기저항로는 그 발열체(heating element)에 따라 최고 사용온도가 다르며 취급법도 다르다. Silicon carbide로는 그 발열체가 Sic(carborundum) 입자의 소결체로서 붕상 또는 ribbon상으로 상품화되어 있다. 제조회사에 따라 각각 다른 trade name(즉, Elemer, Globar, Siliconit)으로 불리워지고 있다. 이 발열체를 사용하는 로는 NI-Cr로 보다 높은 온도, 즉 1500℃까지 쓸 수 있으나, 소결체이므로 기계적으로나 열적 shock에 약하며, 고온에서 장시간 상요하면 발열체의 산화로 수명이 단축되는 문제점들이 있다. 기타 발열체로는 Pt, Ta, Mo, W 등 내열금속과 합금들을 사용하는 예들도 있다. 이밖에도 고온로로서는 고주파로, 저주파로, arc로, gas로, 크립틀로 등 다양하다.

1.3 열전대의 기본 원리와 정의
1821년 제베크(Thomas Johann Seebeck)는 두 종류의 금속 A, B를 접합하고, 양 접점에 온도를 달리 해주면 온도차에 비례하여 열기전력이 생긴다는 것을 발견했다. 한쪽 접촉점을 기준점으로 삼고 측정하고자 하는 부위에 다른 접촉점을 위치하면 기전력의 크기로 온도차를 알 수 있으므로 기준점의 온도와 비교하여 온도를 측정하게 된다.
보통 기준 접촉점은 온도가 일정하여 기준접점이라 하고, 측정하고자 하는 곳에 위하는 접촉점을 측온접점이라 부른다. 온도가 기전력의 크기로 나타나므로 이를 전기 신호로 증폭할 수 있어 측정이 용이하다. 열전대와 열전대의 기전력으로 온도를 환산하는 장치간에 거리가 멀어도 되며 회로 도중의 온도 변화는 측정치에 거의 영향을 주지 않는다. 정밀도에 비해 가격이 싸며. 넓은 온도 범위 측정이 가능하다.